Cossa Polimeri ESTALUX 9206 Methyl Methacrylate Acrylonitrile Butadiene Styrene

Category	Polymer , Thermoplastic , ABS Polymer , Acrylic (PMMA)
Manufacturer	Cossa Polimeri S.r.L.
Trade Name	ESTALUX
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Cossa Polimeri ESTALUX 9206 Methyl Methacrylate Acrylonitrile Butadiene Styrene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Plastic blend that combines impact properties of ABS with the excellent transparency of PMMABiomedical grade in line with US pharmacopeia class VI USP and European pharmacopeia cap. 3.2.2Information provided by Cossa Polimeri S.r.l.

Physical Properties	Metric	English	Comments
Density	1.07 g/cc	0.0387 lb/in³	ASTM D 792
Linear Mold Shrinkage	0.0040 - 0.0070 cm/cm	0.0040 - 0.0070 in/in	ASTM D 955
Melt Flow	6.0 g/10 min @Load 10.0 kg, Temperature 220 °C	6.0 g/10 min @Load 22.0 lb, Temperature 428 °F	ASTM D 1238
	38 g/10 min @Load 21.6 kg, Temperature 220 °C	38 g/10 min @Load 47.6 lb, Temperature 428 °F	ASTM D 1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	30.0 MPa	4350 psi	ASTM D 638
Tensile Strength, Yield	43.0 MPa	6240 psi	ASTM D 638
Elongation at Break	4.0 %	4.0 %	ASTM D 638
Tensile Modulus	1.95 GPa	283 ksi	ASTM D 638
Flexural Modulus	1.80 GPa	261 ksi	ASTM D 790
Izod Impact, Notched	0.600 J/cm @Temperature 23.0 °C	1.12 ft-lb/in @Temperature 73.4 °F	ASTM D 256

Thermal Properties	Metric	English	Comments
Vicat Softening Point	90.0 °C @Load 5.10 kg	194 °F @Load 11.2 lb	120°C/hr; ASTM D 1525
	102 °C @Load 1.02 kg	216 °F @Load 2.25 lb	120°C/hr; ASTM D 1525
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in

Processing Properties	Metric	English
Processing Temperature	220 - 240 °C	428 - 464 °F
Mold Temperature	40.0 - 60.0 °C	104 - 140 °F
Dry Time	2.00 - 4.00 hour @Temperature 80.0 °C	2.00 - 4.00 hour @Temperature 176 °F

Users viewing this material also viewed the following: