Wolf Kunststoff ZEDEX® ZX-324V2T A3F PEEK, PTFE Modified

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, PTFE-Filled
Manufacturer Wolf Kunststoff
Trade Name ZEDEX®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Wolf Kunststoff ZEDEX® ZX-324V2T A3F PEEK, PTFE Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Reduced friction; High wear resistance; High elasticity; Stress resistantApplications: Shipbuilding; Chemical Engineering; Automotive Technology; Machine ToolsInformation provided by Zedex
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
ISO 1183
Water Absorption 0.10 %

@Temperature 23.0 °C
0.10 %

@Temperature 73.4 °F
RMC 93%; DIN EN ISO 62
Moisture Absorption at Equilibrium 0.50 %
0.50 %
DIN EN ISO 62
Mechanical Properties Metric English Comments
Hardness, Shore A 100
100
DIN 53505
Hardness, Shore D 87
87
DIN 53505
Ball Indentation Hardness 175 MPa
25400 psi
DIN 2039
Tensile Strength at Break 90.0 MPa
13100 psi
DIN EN ISO 527
Tensile Strength 92.0 MPa
13300 psi
DIN EN ISO 527
Tensile Stress 26.0 MPa

@Strain 1.00 %,
Time 3.60e+6 sec
3770 psi

@Strain 1.00 %,
Time 1000 hour
DIN 53444
Tensile Strength, Yield 76.0 MPa
11000 psi
Elastic Limit
92.0 MPa
13300 psi
DIN EN ISO 527
Elongation at Break 23.9 %
23.9 %
23.9 %
23.9 %
DIN EN ISO 527
Elongation at Yield 1.5 %
1.5 %
Elastic Yield Point
5.7 %
5.7 %
Flexural; DIN EN ISO 178
6.9 %
6.9 %
Elongation at Maximum Force; DIN EN ISO 527
6.9 %
6.9 %
DIN EN ISO 527
Tensile Modulus 3.50 GPa
508 ksi
DIN EN ISO 527
Flexural Strength 110 MPa
16000 psi
Outer Fiber Stress at 3.5% Outer Fiber Strain; DIN EN ISO 178
127 MPa
18400 psi
DIN EN ISO 178
Flexural Modulus 3.90 GPa
566 ksi
DIN EN ISO 178
Compressive Yield Strength 103 MPa
14900 psi
DIN EN ISO 604
Compressive Strength 76.0 MPa
11000 psi
Elastic Limit
103 MPa
14900 psi
DIN EN ISO 604
35.0 MPa

@Time 3.60e+7 sec
5080 psi

@Time 10000 hour
67.0 MPa

@Time 360000 sec
9720 psi

@Time 100 hour
81.0 MPa

@Time 36.0 sec
11700 psi

@Time 0.0100 hour
80.0 MPa

@Strain 3.50 %
11600 psi

@Strain 3.50 %
DIN EN ISO 604
Compressive Modulus 2.54 GPa
368 ksi
DIN EN ISO 604
Fatigue Strength 56.0 MPa

@# of Cycles 1.00e+6
8120 psi

@# of Cycles 1.00e+6
1 Hz
K Factor (ISO) 1.4 µm/km

@Temperature 100 °C
1.4 µm/km

@Temperature 212 °F
4.8 µm/km

@Temperature 200 °C
4.8 µm/km

@Temperature 392 °F
6.4 µm/km

@Temperature 240 °C
6.4 µm/km

@Temperature 464 °F
12.1 µm/km

@Temperature 20.0 °C
12.1 µm/km

@Temperature 68.0 °F
Charpy Impact Unnotched NB
NB
EN ISO 179/1eU
Charpy Impact, Notched 0.630 J/cm²
3.00 ft-lb/in²
EN ISO 179/1eA
Coefficient of Friction, Dynamic 0.090

@Temperature 100 °C
0.090

@Temperature 212 °F
Dry Operation
0.16

@Temperature 20.0 °C
0.16

@Temperature 68.0 °F
Dry Operation
Coefficient of Friction, Static 0.13

@Temperature 20.0 °C
0.13

@Temperature 68.0 °F
Dry Operation
Tensile Creep Modulus, 1000 hours 2500 MPa
363000 psi
At 1% Deformation; DIN 53444
Limiting Pressure Velocity 0.46666 MPa-m/sec
13323 psi-ft/min
v = 100m/min
0.500 MPa-m/sec
14300 psi-ft/min
v = 200m/min
0.66666 MPa-m/sec
19033 psi-ft/min
v = 10m/min
1.0355 MPa-m/sec
29564 psi-ft/min
v = 1m/min
Compression Set 3.3 %
3.3 %
Elastic Compression Limit
5.4 %
5.4 %
Nominal Compressive Yield Strain; DIN EN ISO 604
5.4 %
5.4 %
Nominal Compressive Strain at Compressive Strength; DIN EN ISO 604
Thermal Properties Metric English Comments
CTE, linear 62.0 µm/m-°C

@Temperature <=100 °C
34.4 µin/in-°F

@Temperature <=212 °F
ISO E 830
65.0 µm/m-°C

@Temperature <=150 °C
36.1 µin/in-°F

@Temperature <=302 °F
ISO E 831
Specific Heat Capacity 1.05 J/g-°C
0.251 BTU/lb-°F
DSC
Melting Point 340 °C
644 °F
DSC
Maximum Service Temperature, Air 115 °C
239 °F
Pressed Bushings
250 °C
482 °F
Continuous
260 °C
500 °F
Short Term (3h)
Deflection Temperature at 1.8 MPa (264 psi) 171 °C
340 °F
DIN EN ISO 75
Glass Transition Temp, Tg 146 °C
295 °F
DSC
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 6.00e+16 ohm-cm
6.00e+16 ohm-cm
IEC 93
Surface Resistance 6.80e+12 ohm
6.80e+12 ohm
IEC 93
Dielectric Constant 3.3

@Frequency 110 Hz
3.3

@Frequency 110 Hz
IEC 250
Dielectric Strength 27.0 kV/mm
686 kV/in
IEC 243
Dissipation Factor 0.0020
0.0020
IEC 112
0.061

@Frequency 1.00 Hz
0.061

@Frequency 1.00 Hz
Descriptive Properties Value Comments
Alignment Adjustment 4
Nominal Scale: 1, low; 10, high
Chemical Sterilization 10
Nominal Scale: 1, low; 10, high
Color Beige
Creep Resistance 5
Nominal Scale: 1, low; 10, high
Dimensional Stability with Thermal Expansion 5
Nominal Scale: 1, low; 10, high
FDA Compliant Applicable
Free from Silicon Applicable
Gamma-rays Radiation Sterilization 7
Nominal Scale: 1, low; 10, high
High Precision Bushings (negative clearance) Applicable
Injection Molded Parts Applicable
Machined Parts Applicable
Moist Heat Sterilization 10
Nominal Scale: 1, low; 10, high
Plastic Granules Applicable
Resistance Against dust, Dirt, Abrasive Substances 7
Nominal Scale: 1, low; 10, high
Resistance Against Hot Water 200
Resistance to Chemicals 9
Nominal Scale: 1, low; 10, high
Resistant Against Disinfectant Applicable
Rods up to Øe (de) Applicable
ROHS/WEEE Applicable
Sheets up to Maximum Thickness Applicable
Sliding Velocity 200
Suitable for Outdoor Use 7
Nominal Scale: 1, low; 10, high
Suitable for Use in Water Applicable
Suitable for Vacuum Applicable
Tubes (hollow rods) up to Øe (de) Applicable
UV Rays Resistance 9
Nominal Scale: 1, low; 10, high
UV-Sterilization 7
Nominal Scale: 1, low; 10, high