EVALCA EVAL® F100 Ethylene Vinyl Alcohol Copolymer Resin (discontinued **)

Category	Polymer , Thermoplastic , Ethylene Vinyl Alcohol (EVOH)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	EVALCA EVAL® F100 Ethylene Vinyl Alcohol Copolymer Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

32 mol % Ethylene.Data provided by EVALCA. Applications: Melt phase forming. EVOH is used in packaging applications because of its outstanding gas barrier properties.EVAL™ is now produced as a part of the Kuraray product line.

Physical Properties	Metric	English	Comments
Density	1.19 g/cc	0.0430 lb/in³	ASTM D1505
Moisture Absorption at Equilibrium	2.2 %	2.2 %	Equilibrium at 50% RH
	2.2 %	2.2 %	50% RH
Water Absorption at Saturation	8.5 %	8.5 %	100% RH
Moisture Vapor Transmission	1.50 cc-mm/m²-24hr-atm	3.81 cc-mil/100 in²-24hr-atm	40°C, 90% RH
Oxygen Transmission	0.00800 cc-mm/m²-24hr-atm	0.0203 cc-mil/100 in²-24hr-atm	20°C; 65% RH; Permeability increases significantly at higher moisture content.
Melt Flow	0.80 g/10 min @Load 2.16 kg, Temperature 190 °C	0.80 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
	1.9 g/10 min @Load 2.16 kg, Temperature 210 °C	1.9 g/10 min @Load 4.76 lb, Temperature 410 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	101	101	ASTM D785
Tensile Strength, Ultimate	74.0 MPa	10700 psi	10%/min; ASTM D638
Tensile Strength, Yield	80.0 MPa	11600 psi	10%/min. ASTM D638
Elongation at Break	130 %	130 %	10%/min. ASTM D638
Elongation at Yield	1.0 %	1.0 %	10%/min. ASTM D638
Modulus of Elasticity	2.60 GPa	377 ksi	Youngs Modulus, ASTM D638, 10%/min.
Flexural Yield Strength	128 MPa	18600 psi	Bending Strength; ASTM D790
Flexural Modulus	4.20 GPa	609 ksi	Bending Elasticity; ASTM D790
Izod Impact, Notched	0.500 J/cm	0.937 ft-lb/in	ASTM D256
Taber Abrasion, mg/1000 Cycles	1.2	1.2	ASTM D1175

Thermal Properties	Metric	English	Comments
CTE, linear	50.0 µm/m-°C	27.8 µin/in-°F	Below Tg
	110 µm/m-°C	61.1 µin/in-°F	Above Tg
Specific Heat Capacity	2.40 J/g-°C	0.574 BTU/lb-°F
Thermal Conductivity	0.340 W/m-K	2.36 BTU-in/hr-ft²-°F	For EVAL F101
Melting Point	183 °C	361 °F	DSC
Deflection Temperature at 0.46 MPa (66 psi)	100 °C	212 °F	For EP-F101
Vicat Softening Point	173 °C	343 °F	For EP-F101
Glass Transition Temp, Tg	69.0 °C	156 °F	Dynamic Viscoelasticity

Optical Properties	Metric	English	Comments
Haze	1.5 %	1.5 %	Estimated by MatWeb from similar grades
Gloss	90 %	90 %	Estimated by MatWeb from similar grades

Electrical Properties	Metric	English	Comments
Dielectric Constant	5.5	5.5	Frequency Not Specified
Dissipation Factor	0.21	0.21	Frequency Not Specified

Processing Properties	Metric	English	Comments
Melt Temperature	<= 240 °C	<= 464 °F