Beijing Chemical Industry KAIFA® MN-401 PA6 Resin
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® MN-401 PA6 Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Good toughnessInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.015 - 0.020 cm/cm | 0.015 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.0 MPa | 6960 psi | ASTM D638 |
| Flexural Strength | 105 MPa | 15200 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 0.690 J/cm @Thickness 3.20 mm |
1.29 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Charpy Impact Unnotched | >= 10.0 J/cm² | >= 47.6 ft-lb/in² | ISO179 |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.9 @Frequency 1e+6 Hz |
2.9 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 22.0 kV/mm @Thickness 2.00 mm |
559 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.029 @Frequency 1e+6 Hz |
0.029 @Frequency 1e+6 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 200 - 210 °C | 392 - 410 °F | |
| Middle Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |
| Front Barrel Temperature | 235 - 245 °C | 455 - 473 °F | |
| Nozzle Temperature | 235 - 240 °C | 455 - 464 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 60.0 - 90.0 MPa | 8700 - 13100 psi |
Users viewing this material also viewed the following:
- P & P Technology Monel-BS3075 (NA13) Knitted Cored Shielding Mesh
- LyondellBasell Petrothene® NA362176 Low Density Polyethylene
- LATI Latene® EP 22UVH2 MX/25 PP Copolymer, Mineral Reinforced
- A. Schulman POLYFORT™ FPP 3716 Talc Filled Copolymer Polypropylene
- Trelleborg Hypalon® H611 Chlorosulphonated Polyethylene
- ExxonMobil Label-Lyte® 15 LLG-101 Clear OPP Film
- Denka VINYKON W1051 PVC, W grade for insulation, for sheaths
- Henkel Hysol EA 9257 Primer
- Lehmann & Voss PLASLUBE NY-1/SI/2/NT Polyamide 66, lubricant modified
Copyright © lookpolymers.com All Rights Reserved