BASF Ultramid® B3WG5 25% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3WG5 25% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: 25% glass-fiber reinforced and heat aging resistant injection-molding grade, for instance, for fan impeller glass-fiber reinforced injection-molding grade for industrial articles and electrical insulating parts.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.500 - 0.800 g/cc
0.0181 - 0.0289 lb/in³
Density 1.32 g/cc
0.0477 lb/in³
ISO 1183
Water Absorption 6.8 - 7.4 %
6.8 - 7.4 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 2.1 - 2.5 %
2.1 - 2.5 %
23°C; 50% RH; ISO 62
2.3 %
2.3 %
50% RH
7.1 %
7.1 %
Saturation
Viscosity Measurement 140
140
ISO 307
Linear Mold Shrinkage 0.0035 cm/cm
0.0035 in/in
restricted
Melt Flow 72.6 g/10 min

@Load 5.00 kg,
Temperature 275 °C
 72.6 g/10 min

@Load 11.0 lb,
Temperature 527 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength 30.0 MPa

@Strain 1.00 %,
Temperature 150 °C
 4350 psi

@Strain 1.00 %,
Temperature 302 °F
 ISO 527
35.0 MPa

@Strain 1.00 %,
Temperature 120 °C
 5080 psi

@Strain 1.00 %,
Temperature 248 °F
 ISO 527
38.0 MPa

@Strain 1.00 %,
Temperature 100 °C
 5510 psi

@Strain 1.00 %,
Temperature 212 °F
 ISO 527
45.0 MPa

@Strain 2.00 %,
Temperature 150 °C
 6530 psi

@Strain 2.00 %,
Temperature 302 °F
 ISO 527
60.0 MPa

@Strain 2.00 %,
Temperature 120 °C
 8700 psi

@Strain 2.00 %,
Temperature 248 °F
 ISO 527
65.0 MPa

@Strain 2.00 %,
Temperature 100 °C
 9430 psi

@Strain 2.00 %,
Temperature 212 °F
 ISO 527
70.0 MPa

@Strain 1.00 %,
Temperature 60.0 °C
 10200 psi

@Strain 1.00 %,
Temperature 140 °F
 ISO 527
83.0 MPa

@Strain 1.00 %,
Temperature 23.0 °C
 12000 psi

@Strain 1.00 %,
Temperature 73.4 °F
 ISO 527
100 MPa

@Strain 1.00 %,
Temperature -20.0 °C
 14500 psi

@Strain 1.00 %,
Temperature -4.00 °F
 ISO 527
100 MPa

@Strain 2.00 %,
Temperature 60.0 °C
 14500 psi

@Strain 2.00 %,
Temperature 140 °F
 ISO 527
143 MPa

@Strain 2.00 %,
Temperature 23.0 °C
 20700 psi

@Strain 2.00 %,
Temperature 73.4 °F
 ISO 527
170 MPa

@Strain 2.00 %,
Temperature -20.0 °C
 24700 psi

@Strain 2.00 %,
Temperature -4.00 °F
 ISO 527
Tensile Strength, Yield 160 MPa
23200 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 3.5 %
3.5 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 8.00 GPa
1160 ksi
ISO 527-1/-2
Flexural Strength 220 MPa
31900 psi
at max force; ISO 178
Flexural Modulus 7.40 GPa
1070 ksi
ISO 178
Izod Impact, Notched (ISO) 12.0 kJ/m²

@Temperature 23.0 °C
 5.71 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/A
Charpy Impact Unnotched 7.50 J/cm²

@Temperature -30.0 °C
 35.7 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
8.00 J/cm²

@Temperature 23.0 °C
 38.1 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
1.20 J/cm²

@Temperature 23.0 °C
 5.71 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 - 25.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 11.1 - 13.9 µin/in-°F

@Temperature 73.4 - 176 °F
 DIN 11359-1/-2
CTE, linear, Transverse to Flow 60.0 - 70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 33.3 - 38.9 µin/in-°F

@Temperature 73.4 - 176 °F
 DIN 11359-1/-2
Specific Heat Capacity 1.50 J/g-°C
0.359 BTU/lb-°F
Thermal Conductivity 0.350 W/m-K
2.43 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 220 °C
428 °F
DIN 53765
Maximum Service Temperature, Air 145 °C
293 °F
for 50% loss of tensile strength after 20000hr
175 °C
347 °F
for 50% loss of tensile strength after 5000hr
200 °C
392 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75-1/-2
Decomposition Temperature >= 300 °C
>= 572 °F
UL RTI, Electrical 130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0591 in
 746B
UL RTI, Mechanical with Impact 95.0 °C

@Thickness 1.50 mm
 203 °F

@Thickness 0.0591 in
 764B
UL RTI, Mechanical without Impact 130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0591 in
 764B
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 3.8

@Frequency 1.00 Hz
 3.8

@Frequency 1.00 Hz
 IEC 60250
Dissipation Factor 0.025

@Frequency 1.00e+6 Hz
 0.025

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 450 V
450 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper Throat
Zone 1 260 °C
500 °F
Feed Zone
Zone 2 270 °C
518 °F
Compression
Zone 3 280 °C
536 °F
Metering-zone
Zone 4 280 °C
536 °F
Nozzle
Melt Temperature 270 - 290 °C
518 - 554 °F
Injection-molding/Extrusion
280 °C
536 °F
Optimal
Mold Temperature 80.0 °C
176 °F
Optimal
80.0 - 90.0 °C
176 - 194 °F
Injection-molding
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.030 - 0.060 %
0.030 - 0.060 %
Optimal
<= 0.15 %
<= 0.15 %
Descriptive Properties Value Comments
Commercial Status Europe
Ignition Temperature >400°C
ASTM D129
Peripheral screw speed < 0.3 m/s