Beijing Chemical Industry KAIFA® GL5200 ABS Extrusion Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® GL5200 ABS Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Non-toxic, Superior impact strength at low temp., High gloss, Uniform sheet thickness for vacuum moldingInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | 24 hr; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ASTM D790 |
| Izod Impact, Notched | 0.460 J/cm @Thickness 3.20 mm |
0.862 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 180 - 230 °C | 356 - 446 °F | Resin Temp. |
| Rear Barrel Temperature | 190 °C | 374 °F | |
| Middle Barrel Temperature | 210 °C | 410 °F | |
| Front Barrel Temperature | 220 °C | 428 °F | |
| Nozzle Temperature | 215 °C | 419 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 - 90.0 °C @Thickness 30.0 mm |
176 - 194 °F @Thickness 1.18 in |
|
| Dry Time | 4 hour @Thickness 30.0 mm |
4 hour @Thickness 1.18 in |
|
| Injection Pressure | 80.0 - 130 MPa | 11600 - 18900 psi | injection speed: 80 - 120 rpm |
| Back Pressure | 1.00 - 2.00 MPa | 145 - 290 psi | Mold Pressure |
| Screw Speed | 100 rpm | 100 rpm |
Users viewing this material also viewed the following:
- PolyOne LubriOne™ ATT-000/5T Black Acetal (POM) Copolymer
- Polimersan Plastics POLIPOM® (POM)
- DuPont Performance Polymers Crastin® SC164 NC010 PBT (Unverified Data**)
- LG Chemical LUPOY GP5006B PC/ABS
- Lubriplate Special Auto Marine Grease Automotive Lubricant
- Lanxess Durethan® DP BM 410 H2.0 901510 Nylon 6, 10% Mineral + Glass Fiber
- A. Schulman INVISION™ VX-5060UI INVISIONTMSoft Touch Polyolefin Thermoplastic
- Trimay® Wear Plate TWP61 Complex-carbide Flux Cored Weld Wire & Electrode
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 2.0 PHR Sulfur
Copyright © lookpolymers.com All Rights Reserved