BASF Ultramid® C3U PA66/6 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, Unreinforced |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® C3U PA66/6 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid C3U is an injection molding, general purpose PA66/6 grade with improved flame retardance.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Water Absorption | 8.0 - 9.0 % | 8.0 - 9.0 % | ISO 62 |
| Moisture Absorption at Equilibrium | 2.6 - 3.2 % | 2.6 - 3.2 % | (23°C/50% R.H.); ISO 62 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | Viscosity number; ISO 307 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | |
| Melt Flow | 162 g/10 min @Load 5.00 kg, Temperature 275 °C |
162 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50mm/min; ISO 527 |
| Elongation at Yield | 20 % | 20 % | 50mm/min; ISO 527 |
| Modulus of Elasticity | 1.50 GPa | 218 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | ISO 180/A |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/1eA |
| Tensile Creep Modulus, 1000 hours | 890 MPa | 129000 psi | ISO 899 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.70 J/g-°C | 0.406 BTU/lb-°F | |
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 243 °C | 469 °F | DIN 53765 |
| Maximum Service Temperature, Air | 107 °C | 225 °F | for 50% loss of tensile strength after 20,000 hr |
| 123 °C | 253 °F | for 50% loss of tensile strength after 5,000 hr | |
| 200 °C | 392 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Constant | 6.0 @Frequency 1.00e+6 Hz |
6.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.30 @Frequency 1.00e+6 Hz |
0.30 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | Test Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | Injection-molding/Extrusion |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection-molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | North America and Europe | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufFlex™ GA-1042FR-60-0-405 Black TPE Compound
- Solvay Specialty Polymers Amodel® A-1115 HS Polyphthalamide (PPA) Resin, 15% Glass Reinforced, at 50% RH (dis
- Lehigh Technologies 200 Mesh Ground Reclaimed Whole Tire Rubber
- Borealis BorECO™ BEC5015 Polypropylene Block Copolymer for Non-Pressure Pipes
- Universal Wire Works 67 Nickel Alloy Welding Wire
- A. Schulman POLYBATCH™ Dark Grey 80431U Concentrate Based In LLDPE
- Applied Composites 8068 Polyester SMC
- 3M Scotch-Weld™ DP-100 Epoxy Adhesive
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 30 PHR N550 (FEF) Filler
Copyright © lookpolymers.com All Rights Reserved