SABIC Innovative Plastics LNP THERMOCOMP Lexan_BFL2200 PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP Lexan_BFL2200 PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
design for black light frame application as high flow PC, V-2, high reflection grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0074 - 0.0076 cm/cm @Thickness 3.20 mm |
0.0074 - 0.0076 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 36.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
36.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 35 g/10 min @Load 1.20 kg, Temperature 300 °C |
35 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 |
| 50.0 MPa | 7250 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | Type I, 5 mm/min; ASTM D638 |
| 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 47.9 % | 47.9 % | 5 mm/min; ISO 527 |
| 59 % | 59 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 5.4 % | 5.4 % | Type I, 5 mm/min; ASTM D638 |
| 5.4 % | 5.4 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.59 GPa | 376 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 84.0 MPa | 12200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.22 GPa | 322 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 5.47 J/cm | 10.2 ft-lb/in | ASTM D256 |
| 1.59 J/cm @Temperature -30.0 °C |
2.98 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1A |
| 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 3.40 J/cm² | 16.2 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 61.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 68.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 68.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 68.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 172 °C | 342 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 144 °C | 291 °F | Rate B/50; ISO 306 |
| 144 °C | 291 °F | Rate B/50; ASTM D1525 | |
| 146 °C | 295 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Huntsman PE5032 Extrusion Coating Polyethylene (discontinued **)
- Mallard Creek Polymers ROVENE® 4201 SBR Emulsion
- LG Chemical Lupoy 1301EP30 Polycarbonate Resin
- Industrial Laminates/Norplex NP424 Laminate
- Johnson Matthey Matti-sil 56Sn Cadmium Free Brazing Alloy
- SABIC Innovative Plastics LNP LUBRILOY D2000 PC (Asia Pacific)
- Techmer ES HiFill® ABS GM30 LE 30% Glass Filled
- Techmer ES Luriblend® PA6/6 GF33 TL10 HS 33% Glass Filled
- Silberline Sparkle Silvet® 760-20-E
- Buckeye Polymers BP FLEX A6810 BLK Thermoplastic Elastomer SEBS
Copyright © lookpolymers.com All Rights Reserved