Sichuan Deyang Haton® hXGR41 Polyphenylene Sulfide
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | Sichuan Deyang Chemical Co. Ltd. |
| Trade Name | Haton® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sichuan Deyang Haton® hXGR41 Polyphenylene Sulfide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection molding, high strengthInformation provided by Sichuan Deyang Chemical Co., LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | GB/T 1033.1-2008 |
| Water Absorption | 0.020 % | 0.020 % | GB/T 1034-2008 |
| Linear Mold Shrinkage, Flow | 0.0038 cm/cm | 0.0038 in/in | GB/T 15585-1995 |
| Linear Mold Shrinkage, Transverse | 0.0088 cm/cm | 0.0088 in/in | GB/T 15585-1995 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 116 MPa | 16800 psi | GB/T 1040.2-2006 |
| Elongation at Break | 3.1 % | 3.1 % | GB/T1040.2-2006 |
| Flexural Strength | 176 MPa | 25500 psi | GB/T 9341-2008 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | GB/T 9341-2008 |
| Izod Impact, Notched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | GB/T 1843-2008 |
| Izod Impact, Unnotched (ISO) | 48.0 kJ/m² | 22.8 ft-lb/in² | GB/T 1843-2008 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 280 °C | 536 °F | GBT/T 19466.3-2004 |
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | GB/T 1634.2-2004 |
| Flammability, UL94 | V-2 | V-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.60e+16 ohm-cm | 4.60e+16 ohm-cm | GB/T1410-2006 |
| Surface Resistivity per Square | 6.00e+15 ohm | 6.00e+15 ohm | GB/T1410-2006 |
| Dielectric Constant | 4.0 | 4.0 | GB/T 1409-2006 |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | GB/T1408.1-2006 |
| Dissipation Factor | 0.0020 | 0.0020 | GB/T 1409-2006 |
Users viewing this material also viewed the following:
- Oceanchem Group Ammonium Bromide Photo Grade I
- Ravago Manufacturing Americas Hylex® P1318LLT Polycarbonate
- Chevron Phillips HiD® 9662 HDPE Blown Film Resin (discontinued **)
- Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes
- Teknor Apex APEX® 2555-H Polyvinyl Chloride, Flexible
- Polyram PlusTek RA334G6 Nylon 6.6, 30% Glass Fiber
- Chevron Phillips K-Resin® KR05NW Styrene-Butadiene Copolymer, Sheet and Blow Mold Grade
- DuPont Teijin Films Melinex® 454 Polyester Film, 400 Gauge
- Ascend Performance Materials Vydyne® 66B, 66J Nylon 66, Dry as Molded
Copyright © lookpolymers.com All Rights Reserved