BASF Ultramid® B3L PA6 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3L PA6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid B3L is an impact-modified, easy flowing injection molding PA6 grade for fast processing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Water Absorption | 8.5 - 9.5 % | 8.5 - 9.5 % | ISO 62 |
| Moisture Absorption at Equilibrium | 2.1 - 2.9 % | 2.1 - 2.9 % | 23°C/50% R.H.; ISO 62 |
| Melt Flow | 121 g/10 min @Load 5.00 kg, Temperature 275 °C |
121 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | 50mm/min; ISO 527 |
| Elongation at Yield | 3.5 % | 3.5 % | 50mm/min; ISO 527 |
| Modulus of Elasticity | 2.80 GPa | 406 ksi | ISO 527 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO180/A |
| 5.50 kJ/m² @Temperature -30.0 °C |
2.62 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A | |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/1eA |
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 - 100 µm/m-°C @Temperature 23.0 - 80.0 °C |
38.9 - 55.6 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | |
| Thermal Conductivity | 0.320 W/m-K | 2.22 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 220 °C | 428 °F | DIN 53762 |
| Maximum Service Temperature, Air | 160 °C | 320 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.010 @Frequency 100 Hz |
0.010 @Frequency 100 Hz |
IEC 60250 |
| 0.024 @Frequency 1.00e+6 Hz |
0.024 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | Test Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | Injection-molding/Extrusion |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Injection molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | North America and Europe | |
| Form | Pellets | |
| Impact Modified | Yes | |
| Primary Processing Technique | Injection Molding | |
| Processing | Injection Molding | |
| Special characteristic | Heat stabilized or stable to heat | |
| Release agent |
Users viewing this material also viewed the following:
- Nyco ASPECT® 3000 Wollastonite
- SABIC Innovative Plastics Lexan® 950A PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics Lexan® FXE101R PC
- Lehmann & Voss LUVOCOM® 1301-0793 PPS, linear, with glass fiber
- SABIC Innovative Plastics NORYL PX9406K PPE+HIPS (Asia Pacific)
- SABIC Innovative Plastics LNP Thermotuf U1000AIS PPA
- ChevronTexaco Delo® 100 Motor Oil, SAE 50
- Azdel SuperLite® SL550900-100 PP Resin Matrix / 55% Glass Fiber (4 mm Molded Thickness)
- Aclo Accutech Polypropylene Homopolymer HP0334C30L Calcium Reinforced
- Ascend Performance Materials Vydyne® R530H Nylon 66, 30% Glass Filled, Dry as Molded
Copyright © lookpolymers.com All Rights Reserved