- PlastiComp Complet® LGF40 - TPU Rigid Thermoplastic Polyurethane, 40% Long Glass Fiber Reinforced
PlastiComp Complet® LGF40 - TPU Rigid Thermoplastic Polyurethane, 40% Long Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Glass Fiber Reinforced |
| Manufacturer | PlastiComp |
| Trade Name | Complēt® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PlastiComp Complet® LGF40 - TPU Rigid Thermoplastic Polyurethane, 40% Long Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Rigid polyurethane with 40% long glass fiber reinforcementInformation provided by PlastiComp, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ASTM D-792 |
| Filler Content | 40 % | 40 % | Long Glass Fiber |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 207 MPa | 30000 psi | ASTM D-638 |
| Elongation at Break | 2.0 - 3.0 % | 2.0 - 3.0 % | ASTM D-638 |
| Tensile Modulus | 11.034 GPa | 1600.3 ksi | ASTM D-638 |
| Flexural Strength | 317 MPa | 46000 psi | ASTM D-790 |
| Flexural Modulus | 11.034 GPa | 1600.3 ksi | ASTM D-790 |
| Izod Impact, Notched | 4.81 J/cm | 9.01 ft-lb/in | ASTM D-256 |
| Izod Impact, Unnotched | 15.49 J/cm | 29.02 ft-lb/in | ASTM D-4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | ASTM D-648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 204 - 227 °C | 400 - 440 °F | |
| Middle Barrel Temperature | 210 - 232 °C | 410 - 450 °F | |
| Front Barrel Temperature | 216 - 238 °C | 420 - 460 °F | |
| Nozzle Temperature | 221 - 243 °C | 430 - 470 °F | |
| Melt Temperature | 216 - 238 °C | 420 - 460 °F | |
| Mold Temperature | 87.8 °C | 190 °F | |
| Injection Velocity | 50.8 - 76.2 mm/sec | 2.00 - 3.00 in/sec | |
| Drying Temperature | 88.0 °C @Time 14400 sec |
190 °F @Time 4.00 hour |
|
| Moisture Content | <= 0.020 % | <= 0.020 % | |
| Back Pressure | 0.172 - 0.345 MPa | 25.0 - 50.0 psi | |
| Cushion | 0.635 cm | 0.250 in | |
| Screw Speed | 30 - 50 rpm | 30 - 50 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Pressure | Medium to maximum |
Users viewing this material also viewed the following:
- NanoAmor 90% Regular Single Walled Carbon Nanotubes
- Ravago Manufacturing Americas Hylex® P1310G30 HB Polycarbonate, 30% Fiberglass Reinforced, UV Stabilized
- Lanxess Durethan® BKV 30 EF 000000 Nylon 6, 30% Glass Fiber
- LATI Larton L K/20 L-PPS, 20% Carbon Fiber Reinforced
- SABIC Innovative Plastics NORYL WCV063 PPE+SEBS+Polyolefin
- SABIC Innovative Plastics LNP LUBRICOMP MX91206 PP
- SABIC Innovative Plastics ULTEM HU2410 PEI
- Silberline Sparkle Silver® 3666
- Thermoseal KLINGERSIL® C-4500 Carbon Fiber Reinforced Gasketing
- CRP Technology Windform® XT Polyamide-Carbon Composite
Copyright © lookpolymers.com All Rights Reserved