BASF Ultramid® B3EG7 BK 00564 35% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3EG7 BK 00564 35% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: 35% Glass fiber reinforced injection molding grade for industrial articles and electrical insulating parts.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.500 - 0.800 g/cc
0.0181 - 0.0289 lb/in³
Density 1.41 g/cc
0.0509 lb/in³
ISO 1183
Water Absorption 5.9 - 6.5 %
5.9 - 6.5 %
ISO 62
Moisture Absorption at Equilibrium >= 2.0 %
>= 2.0 %
50% RH
1.8 - 2.2 %
1.8 - 2.2 %
ISO 62
>= 6.2 %
>= 6.2 %
Saturation
Viscosity Measurement 140
140
ISO 307
Linear Mold Shrinkage 0.0035 cm/cm
0.0035 in/in
Melt Flow 63.45 g/10 min

@Load 5.00 kg,
Temperature 275 °C
 63.45 g/10 min

@Load 11.0 lb,
Temperature 527 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 195 MPa
28300 psi
ISO 527-1/-2
Elongation at Break 3.5 %
3.5 %
ISO 527-1/-2
Tensile Modulus 11.0 GPa
1600 ksi
ISO 527-1/-2
Flexural Strength 280 MPa
40600 psi
ISO 178
Flexural Modulus 10.0 GPa
1450 ksi
ISO 178
Izod Impact, Notched (ISO) 19.0 kJ/m²

@Temperature 23.0 °C
 9.04 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1A
Charpy Impact Unnotched 9.00 J/cm²

@Temperature -30.0 °C
 42.8 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
10.0 J/cm²

@Temperature 23.0 °C
 47.6 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 1.30 J/cm²

@Temperature -30.0 °C
 6.19 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
1.80 J/cm²

@Temperature 23.0 °C
 8.57 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 15.0 - 20.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 8.33 - 11.1 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-1/-2
CTE, linear, Transverse to Flow 60.0 - 70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 33.3 - 38.9 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-1/-2
Thermal Conductivity 0.360 W/m-K
2.50 BTU-in/hr-ft²-°F
DIN 52612-1
Melting Point 220 °C
428 °F
ISO 11357-1/-3
Maximum Service Temperature, Air 135 °C
275 °F
for 50% loss of tensile strength after 20000hr
165 °C
329 °F
for 50% loss of tensile strength after 5000hr
200 °C
392 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
ISO 75-1/-2
Decomposition Temperature >= 300 °C
>= 572 °F
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 3.9

@Frequency 1.00e+6 Hz
 3.9

@Frequency 1.00e+6 Hz
 IEC 60250
Dissipation Factor 0.021

@Frequency 1.00e+6 Hz
 0.021

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 575 V
575 V
Test Solution A; IEC 60112
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper Throat
Zone 1 260 °C
500 °F
Feed Zone
Zone 2 370 °C
698 °F
Compression
Zone 3 280 °C
536 °F
Metering-zone
Zone 4 280 °C
536 °F
Nozzle
Melt Temperature 270 - 290 °C
518 - 554 °F
Injection Molding/Extrusion
280 °C
536 °F
Optimal
Mold Temperature 80.0 °C
176 °F
Optimal
80.0 - 90.0 °C
176 - 194 °F
Injection Molding
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Descriptive Properties Value Comments
Color BK 00564
Commercial Status Europe
Ignition Temperature >400°C
ASTM D1929
Peripheral screw speed < 0.3 m/s