BASF Ultramid® A3K Q601 PA66(Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® A3K Q601 PA66(Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Ultramid A3K Q601 is an easy flowing, injection molding grade PA66.Applications: Typical applications include fast processing high stress technical parts or electrically insulating parts.Information provided by BASF

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	ISO 1183
Moisture Absorption at Equilibrium	2.8 %	2.8 %	50% RH; ISO 62
	8.5 %	8.5 %	Saturation; ISO 62

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	85.0 MPa	12300 psi	ISO 527
Elongation at Break	20 %	20 %	Nominal; ISO 527
Elongation at Yield	5.0 %	5.0 %	ISO 527
Tensile Modulus	3.00 GPa	435 ksi	ISO 527
Flexural Strength	100 MPa	14500 psi	ISO 178
Flexural Modulus	2.90 GPa	421 ksi	ISO 178
Izod Impact, Notched (ISO)	5.50 kJ/m² @Temperature 23.0 °C	2.62 ft-lb/in² @Temperature 73.4 °F	ISO 180
Charpy Impact Unnotched	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179
Charpy Impact, Notched	0.500 J/cm² @Temperature 23.0 °C	2.38 ft-lb/in² @Temperature 73.4 °F	ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	260 °C	500 °F	ISO 3146
Deflection Temperature at 1.8 MPa (264 psi)	75.0 °C	167 °F	ISO 75

Processing Properties	Metric	English
Melt Temperature	280 - 300 °C	536 - 572 °F
Mold Temperature	40.0 - 80.0 °C	104 - 176 °F
Dry Time	2 - 4 hour	2 - 4 hour
Moisture Content	<= 0.20 %	<= 0.20 %

Descriptive Properties	Value	Comments
Color	Q601
Commercial Status	North America