TPI Porene® ABS-SP-100 Super High Impact ABS Resin
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Thai Petrochemical Industry Co. LTD. |
| Trade Name | Porene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | TPI Porene® ABS-SP-100 Super High Impact ABS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Melt Flow | 18 g/10 min @Load 10.0 kg, Temperature 220 °C |
18 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 44.1 MPa @Thickness 3.17 mm |
6400 psi @Thickness 0.125 in |
|
| Flexural Yield Strength | 63.4 MPa @Thickness 3.17 mm |
9200 psi @Thickness 0.125 in |
|
| Flexural Modulus | 2.15 GPa @Thickness 3.17 mm |
312 ksi @Thickness 0.125 in |
|
| Izod Impact, Notched | 3.31 J/cm @Thickness 6.35 mm |
6.20 ft-lb/in @Thickness 0.250 in |
|
| 4.00 J/cm @Thickness 3.17 mm |
7.49 ft-lb/in @Thickness 0.125 in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 °C | 380 °F | |
| Middle Barrel Temperature | 216 °C | 420 °F | |
| Front Barrel Temperature | 227 °C | 440 °F | |
| Melt Temperature | 232 - 260 °C | 450 - 500 °F | Nozzle temp not greater than stock |
| Mold Temperature | 48.9 - 65.6 °C | 120 - 150 °F | |
| Drying Temperature | 87.8 - 93.3 °C | 190 - 200 °F | |
| Dry Time | 2 - 24 hour | 2 - 24 hour | |
| Injection Pressure | 68.9 - 82.7 MPa | 10000 - 12000 psi | |
| Back Pressure | 0.689 MPa | 100 psi | |
| Screw Speed | 50 - 60 rpm | 50 - 60 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Fill Speed | Slow to Moderate |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 6821 C BLK
- IDI Composites E-204 Thermoset Polyester, Sheet
- Johnson Matthey Mattiflux 100 Brazing Flux Paste
- Isoflon Tisoflon® 10G Polytetrafluoroethylene & Graphite Coated Glass Fabric
- SABIC Innovative Plastics PC0703 PC (Europe-Africa-Middle East)
- Borealis Daplen™ EF040AE TPO Compound
- E-Polymers SEPAZ® V220A 20% Glass Fiber Reinforced PPA
- 3M 3361 Stainless Steel Foil Tape
- 3M Scotch-Weld™ DP-100NS Epoxy Adhesive
- Akro-Plastic Akromid® B3 GF 30 S1 BLACK (1281) PA, Cold-Impact Resistant, 30% Glass Filled, Black
Copyright © lookpolymers.com All Rights Reserved