BASF Ultramid® 8202 HS PA6 (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer	BASF
Trade Name	Ultramid®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® 8202 HS PA6 (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid 8202 HS is a heat stabilized, low viscosity, general purpose nylon 6 injection molding homopolymer. It possesses the combination of strength and toughness and has excellent chemical and abrasion resistance. The heat stabilizer system extends the retention of properties at the more elevated temperatures. Excellent in filling thin walls or areas.

Physical Properties	Metric	English	Comments
Density	0.932 g/cc	0.0337 lb/in³	Melt; ISO 1183
	1.13 g/cc	0.0408 lb/in³	dry; ISO 1183
Water Absorption	1.6 %	1.6 %	24 hour; ISO Test
	9.5 %	9.5 %	beginning dry; ISO 62
Moisture Absorption at Equilibrium	2.7 %	2.7 %	beginning dry (23°C/50% R.H.); ISO 62
Relative Viscosity	2.6 cP	2.6 cP	ISO Test; 96 % SAV
Viscosity Measurement	48	48	Formic Acid
Linear Mold Shrinkage	0.012 cm/cm	0.012 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	60.0 MPa	8700 psi	0.2 in/min; ASTM Test
	80.0 MPa @Temperature -40.0 °C	11600 psi @Temperature -40.0 °F	ASTM Test
	80.0 MPa @Temperature -40.0 °C	11600 psi @Temperature -40.0 °F	ISO Data
Tensile Strength, Yield	36.0 MPa	5220 psi	2 in/min; ASTM Test
	36.0 MPa	5220 psi	50mm/min; ISO 527
	20.0 MPa @Temperature 120 °C	2900 psi @Temperature 248 °F	ISO Data
	20.0 MPa @Temperature 120 °C	2900 psi @Temperature 248 °F	ASTM Test
	30.0 MPa @Temperature 80.0 °C	4350 psi @Temperature 176 °F	ASTM Test
	30.0 MPa @Temperature 80.0 °C	4350 psi @Temperature 176 °F	ISO Data
	110 MPa @Temperature -40.0 °C	16000 psi @Temperature -40.0 °F	ASTM Test
	110 MPa @Temperature -40.0 °C	16000 psi @Temperature -40.0 °F	ISO Data
Elongation at Break	>= 50 %	>= 50 %	50mm/min, Nominal strain; ISO 527
	>= 100 %	>= 100 %	2 in/min; ASTM Test
	2.5 % @Temperature -40.0 °C	2.5 % @Temperature -40.0 °F	ASTM Test
	2.5 % @Temperature -40.0 °C	2.5 % @Temperature -40.0 °F	ISO Data
Elongation at Yield	16 %	16 %	50mm/min; ISO 527
	16 %	16 %	2 in/min; ASTM Test
	35 % @Temperature 80.0 °C	35 % @Temperature 176 °F	ASTM Test
	35 % @Temperature 80.0 °C	35 % @Temperature 176 °F	ISO Data
	40 % @Temperature 120 °C	40 % @Temperature 248 °F	ASTM Test
	40 % @Temperature 120 °C	40 % @Temperature 248 °F	ISO Data
Tensile Modulus	0.970 GPa	141 ksi	1mm/min; ISO 527
	0.320 GPa @Temperature 120 °C	46.4 ksi @Temperature 248 °F	ISO Data
	0.550 GPa @Temperature 80.0 °C	79.8 ksi @Temperature 176 °F	ISO Data
	4.00 GPa @Temperature -40.0 °C	580 ksi @Temperature -40.0 °F	ISO Data
Flexural Strength	25.0 MPa	3630 psi	ISO Data
	35.0 MPa	5080 psi	ASTM Test
	154 MPa @Temperature -40.0 °C	22300 psi @Temperature -40.0 °F	ASTM Test
Flexural Modulus	0.740 GPa	107 ksi	ASTM Test
	0.770 GPa	112 ksi	ISO Data
Izod Impact, Notched	0.430 J/cm @Temperature -40.0 °C	0.806 ft-lb/in @Temperature -40.0 °F	ASTM Test
	NB @Thickness 3.17 mm	NB @Thickness 0.125 in	ASTM Test

Thermal Properties	Metric	English	Comments
Specific Heat Capacity	3.728 J/g-°C	0.8910 BTU/lb-°F	Melt
Thermal Conductivity	0.264 W/m-K	1.83 BTU-in/hr-ft²-°F	Melt
Melting Point	220 °C	428 °F	10 K/min

Processing Properties	Metric	English	Comments
Melt Temperature	260 °C	500 °F	Injection molding
Mold Temperature	80.0 °C	176 °F	Injection molding

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	Active America
Form	Pellets
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding
Special characteristic	Heat stabilized or stable to heat
UL.UL-C	Yes