- Polymer Property : Tensile Strength, Yield = 5220 psi
Polymer Property : Tensile Strength, Yield = 5220 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Geloy XTWE270M ASA+SAN (Asia Pacific) Excellent weatherability, good flow/aesthetics and good impact.Profile co-extrusion grade over ABS, PVC or other compatible polymers. XTWE270M is available in various colours.This data was supplied.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Geloy XTWE270M ASA+SAN (Asia Pacific) Excellent weatherability, good flow/aesthetics and good impact.Profile co-extrusion grade over ABS, PVC or other compatible polymers. XTWE270M is available in various colours.This data was supplied.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Ineos Nova 4214 Medium Impact Polystyrene
(discontinued **) Excellent balance of properties, USP Class VIApplications: Consumer electronics, Injection molding applicationsProperties were determined on injection molded specimens at 23°C and 50% R.H. unless o.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Ineos ABS Lustran® QE 1094 AS General Purpose, High-Impact
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionLANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under a JV with La.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 2 in/min; ASTM D638 |
| BASF Capron® 8200 NL Nylon 6 (Conditioned)
(discontinued **) Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Ineos H03G-00 Polypropylene Homopolymer Suggested fabrication methods: ExtrusionFeatures: Low water carry-overTypical applications: Woven fabric, Cordage, Slit filmComplies with FDA specification, Title 21, CFR 177.1520.Typical property d.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50 mm/min; ISO 527-1,-2 |
| Inno-Comp INNOPOL® CS 1-3000 N DEL Polypropylene Homopolymer INNOPOL® CS 1-3000 N DEL is developed for producing injection molded automotive components.All information provided by INNO-COMP. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638-02 |
| Ipiranga Petrochem PH 0130 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638-02 |
| Ipiranga Petrochem PH 0241 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| IRPC Polimaxx Polene 1100RC Polypropylene Homopolymer CHARACTERISTICS: HIGH FLOW, GOOD STIFFNESS, GOOD PROCESSABILITY, GOOD MELT STABILITYAPPLICATIONS: INJECTION MOLDING FOR THIN WALL PARTS, HOUSE WARES EXTRUSION COATING FOR COATED WOVEN BAGS AND TARPA.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| IRPC Polimaxx Polene 1100PK Polypropylene Homopolymer CHARACTERISTICS: HIGH FLOW, GOOD STIFFNESS, GOOD PROCESSABILITY, GOOD MELT STABILITYAPPLICATIONS: MULTI - FILAMENT FOR BELTS, FIBRES FOR CARPETS INJECTION MOLDING FOR THIN WALL PARTS, HOUSEWARES |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP MX91206 PP LNP* Lubricomp* MX91206 is a compound based on Polypropylene containing proprietary fillers. Added feature of this grade is: Wear Resistant. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics SABIC PPCOMPOUND 19T1020 PP SABIC® PPcompound 19T1020 is a general purpose, talc filled, heat stabilized homopolymer polypropylene compound. This compound exhibits high flow and is suitable for injection molding application.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP M7001XXH PP LNP* THERMOCOMP* M7001XXH is a compound based on Polypropylene resin containing proprietary antimicrobial additves. Designed for touch surfaces in patient critical healthcare applications. Added f.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50mm/min; ISO 527-2 |
| Borealis HH315MO Polypropylene HH315MO is a polypropylene homopolymer intended for injection molding. Its high melt flow makes it especially suitable for products with long flow length. This grade is designed for high-speed injec.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| UBE UMERIT 2500F Metallocene LLDPE Description: UBE Super Polyethylene Umerit® is an ethylene-olefin copolymer made by UBE using the metallocene catalytic method. The metallocene catalytic method results in superior physical propert.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| UBE UMERIT 2525F Metallocene LLDPE Description: UBE Super Polyethylene Umerit® is an ethylene-olefin copolymer made by UBE using the metallocene catalytic method. The metallocene catalytic method results in superior physical propert.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| A. Schulman POLYFORT™ FPP 1607 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1607 is a 30% talc filled homopolymer polypropylene compound. Information provided by A. Schulman. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ISO 527-2 |
| Total PPH 9040 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 9040 is a nucleated homopolymer. PPH 9040 is characterized by an improved rigidity and high clarity .ApplicationATOFINA Polypropylene PPH 9040 is suitable for the injectio.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50 mm/min; ASTM D638 |
| A. Schulman PP 3369-01 Polypropylene Medium-Flow Homopolymer Polypropylene DescriptionPolypropylene PP 3369-01 is a medium-flow homopolymer polypropylene nucleated and anti-static designed for the molding of thin walled, and large parts.ApplicationTypical applications of P.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 86% Ret. |
| UBE UBESTA® 3030U Nylon 12 (After Saturate Sodium Chloride for 500 hours) Description: UBESTA has a strong resistance to chemicals. Under normal conditions, it is not significantly affected by alkalis, alcohols, ethers, ketones, hydrocarbons, lubricating oils, gasoline, c.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D 638 |
| Cossa Polimeri ESTADIENE 2506 Acrylonitrile Butadiene Styrene ABS for sheet and profile extrusionHigh impact resistance, excellent heat resistance, excellent dimensional stability and processabilityInformation provided by Cossa Polimeri S.r.l. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Aclo Accutech Polypropylene Homopolymer HP0336W10L Wollastonite Reinforced |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM-D638 |
| Braskem PH 0950 HOMO Polypropylene Homopolymer PH 0950 is a medium melt flow rate homopolymer with an antiblocking agent. PH 0950 is specially designed for twisted films produced by cast or blown film extrusion. It exhibits excellent optical pro.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Ineos Nova 4210 Medium Impact Polystyrene
(discontinued **) Excellent balance of properties, USP Class VIApplications: Consumer electronics, Injection molding applicationsProperties were determined on injection molded specimens at 23°C and 50% R.H. unless o.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50mm/min; ISO 527-2 |
| Borealis MD231U Polypropylene Compound, Mineral Filled MD231U is a 20 % mineral filled polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties and a medium melt flow rate. Applications: Air duc.. |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOTUF W1000I PBT (Europe-Africa-Middle East) LNP* THERMOTUF* W1000I is a compound based on Polybutylene Terephalate resin. Added features include: High Impact |
|||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ISO R527 |
| Fainplast Compounds RE 236 Rigid PVC, Extrusion Electric channels |
|||