Polymer Property : Tensile Strength, Yield = 36.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 36.0 MPa
5220 psi
ASTM D638
SABIC PP 510P Polypropylene Homopolymer for Fiber Applications
Product Description: PP 510P is a homopolymer specially designed for fiber extrusion applications with the following features:Consistent processabilityGood thread line stabilityGood color consisten..
Tensile Strength, Yield 36.0 MPa

@Temperature 23.0 °C
5220 psi

@Temperature 73.4 °F
ISO 527
DuPont Performance Polymers Crastin® ST820 BK503 PBT  (Unverified Data**)
Crastin® ST820 BK503 is an unreinforced, Super Tough, black polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Tensile Strength, Yield 36.0 MPa
5220 psi
ASTM D638
Ineos Nova Zylar® 221 Clear Impact Modified Acrylic Copolymer  (discontinued **)
Features: High clarityEnhanced mold releaseGood elongationStyrenic processing advantagesExcellent property retention after ETO and gamma sterilization Applications: DisplaysMedical devicesOffice acc..
Tensile Strength, Yield 36.0 MPa
5220 psi
ASTM D638
Chevron Phillips HiD® 9706 HDPE Injection Molding Resin  (discontinued **)
Resin Type: linear homopolymerCharacteristics: moderate flow, good impact strength, excellent stiffness, good ESCR, moderate shrinkage resistanceApplications: crates and totes, structural foamInform..
Tensile Strength, Yield 36.0 MPa
5220 psi
2 in/min; ASTM D638
BASF Capron® 8202 NL Nylon 6 (Conditioned)  (discontinued **)
Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Tensile Strength, Yield 36.0 MPa
5220 psi
ASTM D638
Flint Hills P5L2K-055 Polypropylene Random Copolymer
Features: Excellent clarity. Product does not contain animal derived components. Phthalate-free.Applications: Injection molding: extrusion blow molding, injection blow molding, stretch blow moldin..
Tensile Strength, Yield 36.0 MPa
5220 psi
ASTM D638
Ineos H05M-00 Polypropylene Homopolymer
Grade H05M-00 is a general purpose polypropylene homopolymer for injection molding applications. This resin provides good long-term heat stability. This material meets the requirements of the Food..
Tensile Strength, Yield 36.0 MPa
5220 psi
ASTM D638-02
Ipiranga Petrochem PH 0130 Polypropylene
The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr..
Tensile Strength, Yield 36.0 MPa
5220 psi
ASTM D638
LyondellBasell Higlass SB224-1 Polypropylene Copolymer, 10% Glass Fiber
Key Features: conventional melt flow, medium modulus, chemically coupled, glass fiber-reinforced polypropylene copolymer, excellent impact strength, good processabilityApplications: automotive wheel..
Tensile Strength, Yield 36.0 MPa
5220 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP MX91206 PP
LNP* Lubricomp* MX91206 is a compound based on Polypropylene containing proprietary fillers. Added feature of this grade is: Wear Resistant.
Tensile Strength, Yield 36.0 MPa
5220 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON FX98501 PE
LNP* STAT-KON* FX98501 is a compound based on Polyethylene resin containing Proprietary Fillers. Added feature of this material is: Electrically Conductive.
Tensile Strength, Yield 36.0 MPa
5220 psi
ISO 527
SABIC Innovative Plastics LNP Stat-loy A3000Z ABS
LNP* Stat-loy* A3000Z is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for t..
Tensile Strength, Yield 36.0 MPa
5220 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP AX06437 ABS
LNP* THERMOCOMP* AX06437 is a compound based on ABS resin containing Proprietary Filler(s). Added feature of this grade is: Platable.
Tensile Strength, Yield 36.0 MPa
5220 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP AX08306 ABS
LNP* THERMOCOMP* AX08306 is a compound based on ABS resin containing Proprietary Filler(s). Added feature of this grade is: Platable.
Tensile Strength, Yield 36.0 MPa
5220 psi
2 in/min; ASTM Test
Styrolution Terblend® N NM-12 ABS/PA6 (Conditioned)
Terblend N NM-12 is an ABS/PA6 blend combining high impact strength and rigidity with an excellent processability and surface appearance.Information provided by STYROLUTION, which is a joint venture..
Tensile Strength, Yield 36.0 MPa
5220 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP M7001XXH PP
LNP* THERMOCOMP* M7001XXH is a compound based on Polypropylene resin containing proprietary antimicrobial additves. Designed for touch surfaces in patient critical healthcare applications. Added f..
Tensile Strength, Yield 36.0 MPa
5220 psi
50mm/min; ISO 527-2
Borealis BE50-7032 Polypropylene Homopolymer for Non-Pressure pipes and extruded sheets
BE50-7032 is a high molecular weight, low melt flow rate polypropylene homopolymer characterized by high stiffness, high heat distortion temperature and high resistance to thermal aging. The materia..
Tensile Strength, Yield 36.0 MPa
5220 psi
50 mm/min; ASTM D638
A. Schulman PP 3369-01 Polypropylene Medium-Flow Homopolymer Polypropylene
DescriptionPolypropylene PP 3369-01 is a medium-flow homopolymer polypropylene nucleated and anti-static designed for the molding of thin walled, and large parts.ApplicationTypical applications of P..
Tensile Strength, Yield 36.0 MPa
5220 psi
ASTM D638
A. Schulman POLYFLAM™ FPP 1006 Talc Filled Homopolymer Polypropylene
DescriptionPolyfort® FPP 1006 is a 20% talc filled homopolymer polypropylene compound.Information provided by A. Schulman.
Tensile Strength, Yield 36.0 MPa
5220 psi
50 mm/min; ASTM D638
A. Schulman PP 3369-01 Polypropylene Medium-Flow Homopolymer Polypropylene
DescriptionPolypropylene PP 3369-01 is a medium-flow homopolymer polypropylene nucleated and anti-static designed for the molding of thin walled, and large parts.ApplicationTypical applications of P..
Tensile Strength, Yield 36.0 MPa
5220 psi
ASTM D638
A. Schulman POLYFORT™ FPP 1607 Talc Filled Homopolymer Polypropylene
DescriptionPolyfort® FPP 1607 is a 30% talc filled homopolymer polypropylene compound. Information provided by A. Schulman.
Tensile Strength, Yield 36.0 MPa
5220 psi
50 mm/min; ISO 527
Chi Mei Polylac® PA-709S ABS - Extrusion
Super Impact Extrusion
Tensile Strength, Yield 36.0 MPa
5220 psi
50 mm/min; ASTM D638
Carmel Olefins CAPILENE® U 77 A Polypropylene Homopolymer
Description: CAPILENE® U 77 A is a high melt flow rate homopolymer for injection molding of products with long flow length. It is specially formulated with antistatic and nucleating additives, al..
Tensile Strength, Yield 36.0 MPa
5220 psi
ASTM-D638
Braskem PH 0950 HOMO Polypropylene Homopolymer
PH 0950 is a medium melt flow rate homopolymer with an antiblocking agent. PH 0950 is specially designed for twisted films produced by cast or blown film extrusion. It exhibits excellent optical pro..
Tensile Strength, Yield 36.0 - 54.0 MPa
5220 - 7830 psi
Average value: 44.1 MPa Grade Count:19
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Plating Grade
This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Plating Grade". Each property range of values reported is minimum..
Tensile Strength, Yield 36.0 MPa
5220 psi
ASTM D638
A. Schulman POLYFLAM™ FPP 1006S Talc Filled Homopolymer Polypropylene
DescriptionPolyfort® FPP 1006S is a 20% talc filled homopolymer polypropylene compound formulated with an internal mold release. Information provided by A. Schulman.
Tensile Strength, Yield 36.0 - 110 MPa
5220 - 16000 psi
Average value: 76.5 MPa Grade Count:111
Overview of materials for Polypropylene with 30% Glass Fiber Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are i..
Tensile Strength, Yield 36.0 MPa
5220 psi
ASTM D638
Ineos H28U-00 Polypropylene Homopolymer  (discontinued **)
Suggested fabrication methods: Injection moldingFeatures: Radiation stableTypical applications: MedicalComplies with FDA specification, Title 21, CFR 177.1520.Typical property data below from inject..