BASF Ultraform® N2520 L POM
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | BASF |
| Trade Name | Ultraform® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultraform® N2520 L POM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Is a POM, product having reduced electric surface resistance.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.850 g/cc | 0.0307 lb/in³ | |
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Water Absorption | 0.80 % | 0.80 % | Saturation; ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.021 cm/cm | 0.021 in/in | ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.021 cm/cm | 0.021 in/in | ISO 2577 |
| Melt Flow | 9.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 120 MPa @Load 36.5 kg, Time 30.0 sec |
17400 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min; ISO 527-2 |
| Elongation at Break | 10 % | 10 % | Nominal, 50 mm/min; ISO 527-2 |
| Elongation at Yield | 7.5 % | 7.5 % | 50 mm/min; ISO 527-2 |
| Modulus of Elasticity | 2.40 GPa | 348 ksi | ISO 527-2 |
| Charpy Impact Unnotched | 2.20 J/cm² @Temperature -30.0 °C |
10.5 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.250 J/cm² @Temperature -30.0 °C |
1.19 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 120 µm/m-°C @Temperature 23.0 - 55.0 °C |
66.7 µin/in-°F @Temperature 73.4 - 131 °F |
DIN 53752 |
| Melting Point | 166 °C | 331 °F | DIN 53765 |
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75-2 |
| Vicat Softening Point | 150 °C | 302 °F | ISO 306 |
| Decomposition Temperature | >= 240 °C | >= 464 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 ohm-cm | 1000 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+7 ohm | 1.00e+7 ohm | IEC 60093 |
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.39 @Frequency 100 Hz |
0.39 @Frequency 100 Hz |
IEC 60250 |
| 0.53 @Frequency 1.00e+6 Hz |
0.53 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F | Hopper Throat |
| Zone 1 | 205 °C | 401 °F | Feed zone |
| Zone 2 | 205 °C | 401 °F | Compression |
| Zone 3 | 210 °C | 410 °F | Metering-zone |
| Zone 4 | 210 °C | 410 °F | Nozzle |
| Melt Temperature | 190 - 220 °C | 374 - 428 °F | Injection-molding |
| 210 °C | 410 °F | Optimal | |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | Injection-molding |
| 100 °C | 212 °F | Optimal | |
| Drying Temperature | 100 °C | 212 °F | |
| Dry Time | 3 hour | 3 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Europe | |
| Ignition Temperature | 320 - 340°C | ASTM D1929 |
| Peripheral screw speed | <0.3 m/s | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- MV Labs GD400 GdCl3·6H2O Gadolinium chloride hexahydrate
- Nilit Nilitop BT G4 FR C3 is a 20% Glass Fiber Reinforced, Flame Retardant PBT
- Lucent Polymers CPP-120 Polypropylene Homopolymer, 20% Calcium Carbonate Filled
- Sharadaa Ceramics HA 70 High Alumina Brick
- Wanhua Chemical Wanthane® WHT-6236 TPU Hot-Melt Adhesive
- Dow AFFINITY™ PL 1845 Polyolefin Plastomer
- Abatron MasterMold 12-8 Flexible Mold Making Compound
- Braskem CP 405XP Compression Molding Polypropylene Heterophasic Copolymer
- Colorite Polymers 7811 Clear Extrusion Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved