- Loxim 820 02C HB Polypropylene Compound, 20% Calcite Filled, Flame Retardant
Loxim 820 02C HB Polypropylene Compound, 20% Calcite Filled, Flame Retardant
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Calcium Carbonate (CaCO3) Filler , Polypropylene, Flame Retardant |
| Manufacturer | Loxim Industries |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Loxim 820 02C HB Polypropylene Compound, 20% Calcite Filled, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Loxim Industries
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.00 - 1.10 g/cc | 1.00 - 1.10 g/cc | ASTM D792 |
| Filler Content | 20 % | 20 % | |
| Linear Mold Shrinkage | 0.015 - 0.017 cm/cm | 0.015 - 0.017 in/in | ASTM D1299 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 25.0 - 27.0 MPa | 3630 - 3920 psi | ASTM D683 |
| Flexural Modulus | 1.50 - 1.70 GPa | 218 - 247 ksi | ASTM D790 |
| Izod Impact, Notched | 0.300 - 0.400 J/cm | 0.562 - 0.749 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 105 - 110 °C | 221 - 230 °F | ASTM D1525, HDT Method B |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- Polimeri Europa Flexirene® MS 20 A Linear Low Density Polyethylene
- SABIC Innovative Plastics Lexan® 201R PC (Asia Pacific)
- SABIC Innovative Plastics LNP FARADEX NS003 PC+ABS (Asia Pacific)
- A. Schulman POLYBATCH™ Hot Sauce Red 50323/2 Concentrate Based In LLDPE
- American Polymers API 375 Polystyrene
- Ascend Performance Materials Vydyne® R535H NT651 Nylon 66, 35% Glass Reinforced, DAM
- ExxonMobil Escorene® LD-712 High EVA Film Resin (discontinued **)
- Arlon 44278R018 0.018" Uncured/Cured/Uncured Silicone Rubber Laminate with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved