Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

BASF Ultraform® N2320 0035 POM

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer BASF
Trade Name Ultraform®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultraform® N2320 0035 POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Rapidly solidifying standard grade for injection molding.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.890 g/cc
0.0322 lb/in³
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Water Absorption 0.80 %
0.80 %
ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
ISO 62
Linear Mold Shrinkage, Flow 0.0021 cm/cm
0.0021 in/in
ISO 2577
Linear Mold Shrinkage, Transverse 0.0021 cm/cm
0.0021 in/in
ISO 2577
Melt Flow 10.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
 10.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 130 MPa

@Load 36.5 kg,
Time 30.0 sec
 18900 psi

@Load 80.5 lb,
Time 0.00833 hour
 ISO 2039-1
Tensile Strength, Yield 63.0 MPa
9140 psi
50 mm/min; ISO 527-1/-2
Elongation at Break 33 %
33 %
50 mm/min, Nominal; ISO 527-1/-2
Elongation at Yield 12.5 %
12.5 %
50 mm/min; ISO 527-1/-2
Tensile Modulus 2.45 GPa
355 ksi
ISO 527-1/-2
Charpy Impact Unnotched 23.0 J/cm²

@Temperature -30.0 °C
 109 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
26.0 J/cm²

@Temperature 23.0 °C
 124 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 0.550 J/cm²

@Temperature -30.0 °C
 2.62 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
0.650 J/cm²

@Temperature 23.0 °C
 3.09 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Tensile Creep Modulus, 1000 hours 1000 MPa

@Strain <=0.500 %
 145000 psi

@Strain <=0.500 %
 ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 110 µm/m-°C

@Temperature 23.0 - 55.0 °C
 61.1 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
Melting Point 167 °C
333 °F
ISO 11357-1/-3
Maximum Service Temperature, Air 100 °C
212 °F
Deflection Temperature at 1.8 MPa (264 psi) 100 °C
212 °F
ISO 75-1/-2
Decomposition Temperature >= 240 °C
>= 464 °F
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
IEC 60093
Dielectric Constant 3.8

@Frequency 1.00e+6 Hz
 3.8

@Frequency 1.00e+6 Hz
 IEC 60250
Dissipation Factor 0.0060

@Frequency 1.00e+6 Hz
 0.0060

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 600 V
600 V
Test Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 200 °C
392 °F
Optimal
190 - 230 °C
374 - 446 °F
Injection molding
Mold Temperature 60.0 - 120 °C
140 - 248 °F
Injection molding
90.0 °C
194 °F
Optimal
Drying Temperature 100 °C
212 °F
Dry Time 3 hour
3 hour
Descriptive Properties Value Comments
Commercial Status Europe
Ignition Temperature 320 - 340 °C
ASTM D1929
Primary Processing Technique Injection Molding