Polykemi AB POLYabs S00 AS UV ABS, High Flow, UV-Stabilized, Antistatic

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Polykemi AB
Trade Name POLYabs
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Polykemi AB POLYabs S00 AS UV ABS, High Flow, UV-Stabilized, Antistatic.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
With Flow; ISO 2577
0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
Across Flow; ISO 2577
Melt Index of Compound 22 g/10 min
<br>@Load 5.00 kg,<br> Temperature 230 °C
 22 g/10 min
<br>@Load 11.0 lb,<br> Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 43.0 MPa
<= 6240 psi
ISO/R527
Elongation at Yield 6.0 %
6.0 %
ISO/R527
Flexural Strength <= 75.0 MPa
<= 10900 psi
ISO 178
Flexural Modulus 2.30 GPa
<br>@Temperature 23.0 °C
 334 ksi
<br>@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 1.00 J/cm²
<br>@Temperature -20.0 °C
 4.76 ft-lb/in²
<br>@Temperature -4.00 °F
 ISO 179
1.40 J/cm²
<br>@Temperature 23.0 °C
 6.66 ft-lb/in²
<br>@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 88.0 °C
190 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 77.0 °C
171 °F
120°C/h; ISO 75/1
Vicat Softening Point 100 °C
<br>@Load 5.001 kg
 212 °F
<br>@Load 11.03 lb
 50°C/h; ISO 306
106 °C
<br>@Load 1.00 kg
 223 °F
<br>@Load 2.21 lb
 50°C/h; ISO 306
Flammability, UL94 HB
<br>@Thickness 1.60 mm
 HB
<br>@Thickness 0.0630 in
Glow Wire Test 650 °C
<br>@Thickness 2.00 mm
 1200 °F
<br>@Thickness 0.0787 in
 IEC 695-2-1