BASF Ultradur® B 4040 G6 30% Glass Filled PBT + PET
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET) |
| Manufacturer | BASF |
| Trade Name | Ultradur® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultradur® B 4040 G6 30% Glass Filled PBT + PET.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT + PET, injection-molding grade containing 30% of glass fibers, for industrial parts, rigid, tough and dimensionally stable, for example for program switches, thermostat parts, small-motor housings for vehicles, headlamp frames, cams, automotive windscreen wiper arms, PCBs, housings, consoles, contact mounts and covers.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.600 - 0.900 g/cc | 0.0217 - 0.0325 lb/in³ | |
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 |
| Water Absorption | 0.40 % | 0.40 % | Saturation; DIN 53495/1L |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH |
| Viscosity Measurement | 105 | 105 | [ml/g]; Viscosity number; ISO 1628 |
| 70 @Temperature 290 °C |
70 @Temperature 554 °F |
20 mins plasticating | |
| 75 @Temperature 280 °C |
75 @Temperature 536 °F |
30 mins plasticating | |
| 75 @Temperature 300 °C |
75 @Temperature 572 °F |
10 mins plasticating | |
| 90 @Temperature 270 °C |
90 @Temperature 518 °F |
30 mins plasticating | |
| 95 @Temperature 290 °C |
95 @Temperature 554 °F |
10 mins plasticating | |
| 100 @Temperature 300 °C |
100 @Temperature 572 °F |
5 mins plasticating | |
| 100 @Temperature 260 °C |
100 @Temperature 500 °F |
30 mins plasticating | |
| 105 @Temperature 280 °C |
105 @Temperature 536 °F |
10 mins plasticating | |
| 106 @Temperature 250 °C |
106 @Temperature 482 °F |
30 mins plasticating | |
| 110 @Temperature 270 °C |
110 @Temperature 518 °F |
10 mins plasticating | |
| 115 @Temperature 260 °C |
115 @Temperature 500 °F |
10 mins plasticating | |
| 115 @Temperature 240 °C |
115 @Temperature 464 °F |
30 mins plasticating | |
| 117 @Temperature 250 °C |
117 @Temperature 482 °F |
10 mins plasticating | |
| 120 @Temperature 240 °C |
120 @Temperature 464 °F |
10 mins plasticating | |
| Linear Mold Shrinkage, Flow | 0.0018 cm/cm | 0.0018 in/in | Sheet |
| Linear Mold Shrinkage, Transverse | 0.0099 cm/cm | 0.0099 in/in | Sheet |
| Melt Flow | 27.9 g/10 min @Load 2.16 kg, Temperature 275 °C |
27.9 g/10 min @Load 4.76 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 145 MPa | 21000 psi | 50 mm/min; ISO 527-2 |
| Elongation at Yield | 2.4 % | 2.4 % | 50 mm/min; ISO 527-2 |
| Modulus of Elasticity | 10.5 GPa | 1520 ksi | ISO 527-2 |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA |
| Dart Drop, Total Energy | 5.00 J | 3.69 ft-lb | W<sub>501</sub> housing; ISO 6603-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.60 J/g-°C | 0.382 BTU/lb-°F | IEC 1006 |
| Melting Point | 220 - 250 °C | 428 - 482 °F | DSC; ISO 11357-3 |
| Maximum Service Temperature, Air | 140 °C | 284 °F | at 50% loss of tensile strength after 20000h; IEC 216-1 |
| 160 °C | 320 °F | at 50% loss of tensile strength after 5000h; IEC 216-1 | |
| 210 °C | 410 °F | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 396 °F | ISO 75-2 |
| Decomposition Temperature | >= 290 °C | >= 554 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Diameter 0.800 mm |
HB @Diameter 0.0315 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 7.40e+15 ohm-cm | 7.40e+15 ohm-cm | IEC 93 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 93 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 250 |
| 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
IEC 250 | |
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | IEC 243/1 |
| Dissipation Factor | 0.0016 @Frequency 100 Hz |
0.0016 @Frequency 100 Hz |
IEC 250 |
| 0.0174 @Frequency 1.00e+6 Hz |
0.0174 @Frequency 1.00e+6 Hz |
IEC 250 | |
| Comparative Tracking Index | 250 V | 250 V | Test solution A; IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat |
| Zone 1 | 260 °C | 500 °F | Feeding zone |
| Zone 2 | 265 °C | 509 °F | Compression |
| Zone 3 | 270 °C | 518 °F | Metering-zone |
| Zone 4 | 270 °C | 518 °F | Nozzle |
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | Injection-molding |
| 270 °C | 518 °F | for shrinkage test, Optimal | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | Injection molding |
| 80.0 °C | 176 °F | for shrinkage test, Optimal | |
| Drying Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Dry Time | 4 hour | 4 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural, Colored, Black and Special Colors | |
| Commercial Status | Europe | |
| Ignition Temperature | 350°C | ASTM D1929 |
| Peripheral screw speed | < 0.25 m/s | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Polikim EFALON® B-60 PTFE, 60% Bronze Filled
- Malvern Minerals Sliastic 740 with 33% Novacite® Daper Quartz Filler
- Karina E 70/236-D-IS Clear PVC Compound
- SABIC Innovative Plastics LNP LUBRICOMP DX94375H PC
- Schott SF1 Glass
- Hexcel® HexForce™ AGP280-5H Carbon Fabric
- Victrex® APTIV® 1300-100G Polyetheretherketone (PEEK) Polymer Film
Copyright © lookpolymers.com All Rights Reserved