Techmer ES HiFillÂ® PA6/6 GF33 BK 33% Glass Filled (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Heat Stabilized
Manufacturer	Techmer ES
Trade Name	HiFill®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Techmer ES HiFillÂ® PA6/6 GF33 BK 33% Glass Filled (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedAppearance: BlackUL File Number: E157318Information provided by TP Composites, Inc.

Physical Properties	Metric	English	Comments
Density	1.37 g/cc	0.0495 lb/inÂ³	ASTM D792
Water Absorption	1.8 % @Time 86400 sec	1.8 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0040 cm/cm @Thickness 3.17 mm	0.0040 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	115	115	ASTM D785
Tensile Strength, Yield	172 MPa	25000 psi	ASTM D638
Elongation at Break	4.2 %	4.2 %	ASTM D638
Flexural Strength	172 MPa	25000 psi	ASTM D790
Flexural Modulus	8.62 GPa	1250 ksi	ASTM D790
Izod Impact, Notched	1.28 J/cm @Thickness 3.17 mm	2.40 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	19.8 Âµm/m-Â°C	11.0 Âµin/in-Â°F	ASTM D696
Melting Point	232 Â°C	450 Â°F
Deflection Temperature at 0.46 MPa (66 psi)	227 Â°C	440 Â°F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	219 Â°C	426 Â°F	Unannealed; ASTM D648
Flammability, UL94	HB	HB

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm	ASTM D257
Dielectric Strength	19.3 kV/mm	490 kV/in	Method A (Short-Time); ASTM D149

Users viewing this material also viewed the following: