- Thermoplastic Polyurethane (TPUR), Polyester Grade
- Huntsman AVALON® 65 DEU Thermoplastic Polyurethane
Huntsman AVALON® 65 DEU Thermoplastic Polyurethane
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | Avalon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman AVALON® 65 DEU Thermoplastic Polyurethane.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: AVALON 65 DEU is a high performance UV-stabilized polyester based thermoplastic polyurethane for injection molding. AVALON 65 DEU is part of the AVALON Perform Range and offers a premium soling material for the sporting goods and fashion markets and is supplied with a high degree of stabilization against premature yellowing from sunlight. The features offered include:UV resistance Excellent surface definitionAbrasion resistanceFlex resistancePhthalate free TPU Information provided by Alliance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 2781 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | ISO 868 |
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ISO 37 |
| Elongation at Break | 300 % | 300 % | ISO 37 |
| 100% Modulus | 0.0240 GPa | 3.48 ksi | ISO 37 |
| 300% Modulus | 0.0330 GPa | 4.79 ksi | ISO 37 |
| Tear Strength | 224 kN/m | 1280 pli | ISO 34B |
| Abrasion | <= 40 | <= 40 | mm<sup>3</sup>; ISO 4649 |
| Compression Set | 25 % | 25 % | ISO 815 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 35.0 °C | 77.0 - 95.0 °F | |
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | |
| Middle Barrel Temperature | 195 - 215 °C | 383 - 419 °F | |
| Front Barrel Temperature | 200 - 220 °C | 392 - 428 °F | |
| Nozzle Temperature | 195 - 210 °C | 383 - 410 °F | |
| Mold Temperature | 25.0 - 50.0 °C | 77.0 - 122 °F | |
| Injection Pressure | 2.00 - 10.0 MPa | 290 - 1450 psi | |
| Hold Pressure | 1.00 - 5.00 MPa | 145 - 725 psi | |
| Back Pressure | 0.0300 - 0.300 MPa | 4.35 - 43.5 psi | |
| Screw Speed | 20 - 80 rpm | 20 - 80 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Ratio | 2-3:1 | |
| L/D Ratio | 20-25:1 | |
| Typical Screw Diameter | 40-120 nm |
Users viewing this material also viewed the following:
- RheTech Products T10UP100-01 10% Talc Reinforced Polypropylene Copolymer, General Purpose Black, UL94 HB Rated
- Osprey Metals Oxygen-Free Electronic Copper Powder (Grade 80% - 22)
- NOVA Chemicals EPS M77B Expandable Polystyrene Resin
- A. Schulman POLYBATCH™ Green 30394 Concentrate Based In LDPE
- CP-Polymer-Technik Wellamid® 6600 MF30 HWCP 30% Milled Glass Fiber Nylon 66, Heat Stabilized, Conditioned
- 3M 2542/Silver Damping Foils
- 3M 41825 Industrial Polyethylene Temporary Surface Protection Tape
- BASF Nypel® 6015G HS BK 15% Glass Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved