Lotte Chemical Titan TITANLENE® LDF260YZ Low density polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Extrusion Grade |
| Manufacturer | Lotte Chemical Titan Holding Sdn. Bhd. (Former Titan Chemicals) |
| Trade Name | TITANLENE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lotte Chemical Titan TITANLENE® LDF260YZ Low density polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LDF260YZ is a low density polyethylene resin for film extrusion. LDF260YZ has no slip and anti-block additives. LDF260YZ meets the U.S. Food and Drug Administration (FDA) criteria for food contact use as specified in 21 CFR 177.1520 (c) 2.1 & (c) 2.2.Applications: Laundry film Textile packaging Produce film Diaper backingAdditives: BarefootAdvantages: Good drawdown Excellent process abilityInformation provided by Titan Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Base Resin Density | 0.922 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| Thickness | 30.0 microns | 1.18 mil | extruded at 2.5:1 BUR |
| Base Resin Melt Index | 5.0 g/10 min | 5.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 250 % | 250 % | ASTM D882 |
| Film Elongation at Break, TD | 440 % | 440 % | ASTM D882 |
| Elmendorf Tear Strength, MD | 9.50 g/micron | 241 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 4.00 g/micron | 102 g/mil | ASTM D1922 |
| Dart Drop | 2.50 g/micron | 63.5 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 19.6 MPa | 2840 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 17.7 MPa | 2570 psi | ASTM D882 |
| 1% Secant Modulus, MD | 186.32 MPa | 27024 psi | ASTM D882 |
| 1% Secant Modulus, TD | 205.94 MPa | 29869 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 93.0 °C | 199 °F | resin; ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 160 - 180 °C | 320 - 356 °F | |
| Blow-up Ratio (BUR) | 2.5 | 2.5 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible G92D Polyvinyl Chloride, Flexible (PVC, Flexible)
- Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded
- Lehmann & Voss LUVOCOM® 1105-7995 PEEK, with carbon fiber
- SABIC Innovative Plastics LNP LUBRICOMP LX91475 PEEK
- Techmer ES HiFill® PA6/6 GF33 HS L BK 33% Glass Filled (Dry)
- Dr. D. Mueller Flexiso® DMD FI 14010 00460 Polyester Electrical Insulation
- Lubrizol ESTANE® 58215 Ether Based Thermoplastic Polyurethane
- Axiall 286FR Moldings & Extrusions Flexible PVC
Copyright © lookpolymers.com All Rights Reserved