Asahi Kasei Xyron® X9653 Modified Polyphenylene Ether
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded |
| Manufacturer | Asahi Kasei |
| Trade Name | Xyron® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Xyron® X9653 Modified Polyphenylene Ether.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AutomotiveInformation provided by Asahi Kasei
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | 23°C; ASTM D792 |
| Moisture Absorption | 0.100 % | 0.100 % | 23°C, 50% RH 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 23°C, 50% RH; ASTM D638 |
| Elongation at Break | 90 % | 90 % | 23°C, 50% RH; ASTM D638 |
| Flexural Strength | 57.0 MPa | 8270 psi | 23°C, 50% RH; ASTM D790 |
| Flexural Modulus | 1.80 GPa | 261 ksi | 23°C, 50% RH; ASTM D790 |
| Izod Impact, Notched | 3.53 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
6.61 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 75.0 µm/m-°C @Temperature -30.0 - 60.0 °C |
41.7 µin/in-°F @Temperature -22.0 - 140 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Equivalant |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Equivalant |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 240 - 290 °C | 464 - 554 °F | Resin Temperature |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |
| Drying Temperature | 90.0 - 100 °C | 194 - 212 °F | Pre-drying Temperature |
| Dry Time | 2 - 4 hour | 2 - 4 hour |
Users viewing this material also viewed the following:
- Nye Lubricants 752 (NG) Synthetic Oil
- MV Labs ZR800 Zr(SO4)2·xH2O Zirconium(IV) sulfate hydrate (low Hf)
- SABIC Innovative Plastics Cycolac® MG47F ABS
- Iran Petrochemical (PCC) SBR-1500 Styrene Butadiene Rubber
- SABIC Innovative Plastics ULTEM LTX300B PEI
- Eurotec® Tecotek® PC44 GR10 GR003 ZG70 PC, 10% glass fiber reinforced, flame retardant - halogen (RoHS compliant), light grey
- Braskem TI4150WR Impact Copolymer Polypropylene
- Bayshore Vinyl Compounds BVC 4200-90 Vinyl Compound
- Trelleborg Z600 Commercial SBR Rubber
- A. Schulman POLYBATCH™ Orange 10334 Concentrate Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved