Asahi Kasei Xyron® X0715 Modified Polyphenylene Ether

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded
Manufacturer Asahi Kasei
Trade Name Xyron®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Asahi Kasei Xyron® X0715 Modified Polyphenylene Ether.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
AutomotiveInformation provided by Asahi Kasei
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
23°C; ASTM D792
Moisture Absorption 0.0900 %
0.0900 %
23°C, 50% RH 24 hours; ASTM D570
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 43.0 MPa
6240 psi
23°C, 50% RH; ASTM D638
Elongation at Break 70 %
70 %
23°C, 50% RH; ASTM D638
Flexural Strength 60.0 MPa
8700 psi
23°C, 50% RH; ASTM D790
Flexural Modulus 1.92 GPa
278 ksi
23°C, 50% RH; ASTM D790
Izod Impact, Notched 2.94 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 5.51 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
CTE, linear 75.0 µm/m-°C

@Temperature -30.0 - 60.0 °C
 41.7 µin/in-°F

@Temperature -22.0 - 140 °F
 ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 113 °C
235 °F
ASTM D648
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
 Equivalant
HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
 Equivalant
Processing Properties Metric English Comments
Processing Temperature 240 - 290 °C
464 - 554 °F
Resin Temperature
Mold Temperature 50.0 - 80.0 °C
122 - 176 °F
Drying Temperature 90.0 - 100 °C
194 - 212 °F
Pre-drying Temperature
Dry Time 2 - 4 hour
2 - 4 hour