Polymer Resources PPX-G15 Modified-PPO, 15% Glass Reinforced, High Flow
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 20% Glass Filled |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PPX-G15 Modified-PPO, 15% Glass Reinforced, High Flow.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Modified-Polyphenylene Oxide, 10% Glass Reinforced, High FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Melt Flow | 1.0 - 8.0 g/10 min @Load 11.6 kg, Temperature 250 °C |
1.0 - 8.0 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 105 | 105 | ASTM D785 |
| Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 |
| Tensile Strength, Yield | 82.7 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Strength | 121 MPa | 17500 psi | ASTM D790 |
| Flexural Modulus | 4.31 GPa | 625 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Temperature 22.8 °C |
1.30 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| 0.908 J/cm @Temperature -30.0 °C |
1.70 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Charpy Impact, Notched | 0.735 J/cm² @Temperature 22.8 °C |
3.50 ft-lb/in² @Temperature 73.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 260 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | ASTM D648 |
| Vicat Softening Point | 141 °C | 285 °F | 120°C/h, 50 N; ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 304 °C | 500 - 580 °F | |
| Middle Barrel Temperature | 271 - 310 °C | 520 - 590 °F | |
| Front Barrel Temperature | 282 - 316 °C | 540 - 600 °F | |
| Melt Temperature | 288 - 316 °C | 550 - 600 °F | |
| Mold Temperature | 71.1 - 104 °C | 160 - 220 °F | |
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0015 |
Users viewing this material also viewed the following:
- Osprey Metals 4340 Low Alloy Steel Powder (Grade 95% - 16)
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 20 PHR Carbon Black, N-990 (MT)
- MetalTek MTEK 87-11-1-0-1 Cast UNS C92500 Gear Bronze
- Supreme Petrochem SC 201LV General Purpose Polystyrene
- UBE UBESTA® 3035JU5 Plasticized Industrial Grade Nylon 12
- Chicago Extruded Metals UNS C36010 Copper-Zinc-Lead Alloy
- Abatron L060330-2 Flexible Polyurea Compound
- 3M FV053 Tire Vinyl Label Products
- Arkema Group Rilsan® AUM 30 T6LD Nylon 12, 30% Glass Bead Filled (Dry)
- A. Schulman ComAlloy Hiloy® 275 Polystyrene Alloy, Mineral Reinforced, Flow Enhanced
Copyright © lookpolymers.com All Rights Reserved