SABIC Innovative Plastics ULTEM 2210K PEI

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM 2210K PEI.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming.
Physical Properties Metric English Comments
Specific Gravity 1.42 g/cc
1.42 g/cc
ASTM D792
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Moisture Absorption 0.550 %
0.550 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 1.0 %
1.0 %
ISO 62
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm

@Thickness 3.20 mm
 0.0030 - 0.0050 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 13 g/10 min

@Load 6.60 kg,
Temperature 337 °C
 13 g/10 min

@Load 14.6 lb,
Temperature 639 °F
 ASTM D1238
Melt Index of Compound 16 g/10 min

@Load 5.00 kg,
Temperature 360 °C
 16 g/10 min

@Load 11.0 lb,
Temperature 680 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 139 MPa
20200 psi
Type I, 5 mm/min; ASTM D638
140 MPa
20300 psi
5 mm/min; ISO 527
Tensile Strength, Yield 139 MPa
20200 psi
Type I, 5 mm/min; ASTM D638
140 MPa
20300 psi
5 mm/min; ISO 527
Elongation at Break 4.0 %
4.0 %
Type I, 5 mm/min; ASTM D638
5.0 %
5.0 %
5 mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
Type I, 5 mm/min; ASTM D638
5.0 %
5.0 %
5 mm/min; ISO 527
Tensile Modulus 6.80 GPa
986 ksi
1 mm/min; ISO 527
6.89 GPa
999 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 210 MPa
30500 psi
2 mm/min; ISO 178
227 MPa
32900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 6.50 GPa
943 ksi
2 mm/min; ISO 178
6.89 GPa
999 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.640 J/cm
1.20 ft-lb/in
ASTM D256
0.640 J/cm

@Temperature -30.0 °C
 1.20 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Unnotched 4.75 J/cm
8.90 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 30.0 kJ/m²
14.3 ft-lb/in²
80*10*4; ISO 180/1U
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 13.0 J

@Temperature 23.0 °C
 9.59 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C

@Temperature -40.0 - 150 °C
 13.9 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
25.0 µm/m-°C

@Temperature 23.0 - 150 °C
 13.9 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature -40.0 - 150 °C
 33.3 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
60.0 µm/m-°C

@Temperature 23.0 - 150 °C
 33.3 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 210 °C

@Thickness 6.40 mm
 410 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
209 °C

@Thickness 3.20 mm
 408 °F

@Thickness 0.126 in
 unannealed; ASTM D648
211 °C

@Thickness 6.40 mm
 412 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 212 °C
414 °F
Rate B/50; ISO 306
218 °C
424 °F
Rate B/120; ISO 306
225 °C
437 °F
Rate B/50; ASTM D1525
Glass Transition Temp, Tg 217 °C
423 °F