Asahi Kasei Xyron® X0700 Modified Polyphenylene Ether
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded |
| Manufacturer | Asahi Kasei |
| Trade Name | Xyron® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Xyron® X0700 Modified Polyphenylene Ether.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AutomotiveInformation provided by Asahi Kasei
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | 23°C; ASTM D792 |
| Moisture Absorption | 0.100 % | 0.100 % | 23°C, 50% RH 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 23°C, 50% RH; ASTM D638 |
| Elongation at Break | 60 % | 60 % | 23°C, 50% RH; ASTM D638 |
| Flexural Strength | 70.0 MPa | 10200 psi | 23°C, 50% RH; ASTM D790 |
| Flexural Modulus | 2.12 GPa | 307 ksi | 23°C, 50% RH; ASTM D790 |
| Izod Impact, Notched | 1.96 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
3.67 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 75.0 µm/m-°C @Temperature -30.0 - 60.0 °C |
41.7 µin/in-°F @Temperature -22.0 - 140 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Equivalant |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Equivalant |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 220 - 250 °C | 428 - 482 °F | Resin Temperature |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |
| Drying Temperature | 90.0 - 100 °C | 194 - 212 °F | Pre-drying Temperature |
| Dry Time | 2 - 4 hour | 2 - 4 hour |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® XCY630 PC+ABS (Asia Pacific)
- SABIC Innovative Plastics Lexan® 950 PC (Europe-Africa-Middle East)
- Indium Corp. Indalloy® 164 Pb-In-Ag Solder Alloy
- Karina 900-35/1-AYR-AC-LF Ivory PVC Compound
- Shuman 502C Black Polypropylene Copolymer
- Teknor Apex Telcar® TL-1472A Thermoplastic Elastomer
- Master Bond EP46HT Epoxy Adhesive for Structural Bonding
- A. Schulman SCHULAMID® 6 GF50H 50% Glass Fiber Reinforced Nylon 6
- A. Schulman POLYFORT™ FPP 1908E Talc Filled Copolymer Polypropylene
- BASF Pluracol® 380 Specialty Polyol
Copyright © lookpolymers.com All Rights Reserved