| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Nylene® Naxel™ AX190 PPE (Polyphenylene Ether) General Purpose Grade. Properties for dry as molded samples.ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75-1/-2 |
| Quadrant EPP Nylatron® MD PA 6 + metal detectable additive, extruded (ISO Data) Metal detectable 6SA grade High wear and fatigue resistance Lower moisture absorption than standard PA6 Metal and visual detection by blue colour Detection by x-ray also possible Continuous use temp.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical AF360S ABS, TBBA-free Flame Retardant, Low Flow Feature: Injection Molding, TBBA-free Flame Retardant, Low FlowApplication: Electric/Electronic Applications (TV, Monitor Housing) IT/OA deviceCAS No. 9003-56-9, 84852-53-9 and 1309-64-4Information .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Ineos Styrenics Avantra® 585K Q402 Rubber Modified Polystyrene Avantra® 585K Q402 is a high-impact grade of polystyrene with extremely high surface gloss and excellent practical toughness. Although Avantra® 585K Q402 can be processed by any method applic.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical TR556 MABS, Transparency, Chemical Resistance Feature: Injection Molding, Transparency, Chemical ResistanceApplication: Sound Proofing Wall, Canopy, Other Transparent SheetsCAS No. 9011-14–7 and 9003-56-9Information provided by LG Chemical.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 6.35 mm |
185 °F @Thickness 0.250 in |
ASTM D648 |
| IRPC Polimaxx Porene SR101 Acrylonitrile Butadiene Styrene Applications:extrusion sheetrefrigerator door liners and inner box linerspicnic coolerssnow boatsluggage cases |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75-1,-2 |
| Lanxess Durethan® BM 240 H3.0 000000 Nylon 6, 40% Mineral PA 6, 40% mineral, injection molding, heat-ageing stabilized, low tendency to warp, isotopic properties |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | |
| LATI Latistat 36/MR-04 ABS Dissipative product based on Acrylonitrile-Butadiene-Styrene copolymer (ABS). Unfilled. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics NORYL SE90 PPE+HIPS (Europe-Africa-Middle East) NORYL SE90 is an unfilled, flame retardant material with a Vicat B/120 of 110°C according ISO 306. NORYL SE90 is V1 at 1.6 mm according UL94 and halogen free according VDE/DIN 472 part 815. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Spartech Noryl® SP-5210 Specialty Sheet Description: Specialty SheetNoryl is a registered trademark of General Electric Company.Information provided by Spartech. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 3.20 mm |
185 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Xenoy® CL402 PBT+PC (Asia Pacific) XENOY CL402 is a high viscosity, unfilled, elastomer modified PC/PBT blend for extrusion/blowmolding applications. ISO1043-label: PC+PBT-I.This data was supplied by SABIC-IP for the Asia Pacific reg.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75 |
| Styrolution PS 495N HIPS Styrolution PS 495N is an impact resistant polystyrene with a good balance of toughness, high flow, heat resistance and high gloss.High flowGood balance of toughness and heat resistanceUL 94 HBInfor.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 3.20 mm |
185 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Verton NV0061EV_GY7E148 PC+ABS Preliminary data for 30% long fiber single pellet non-halogen FR color filled PC/ABSThis data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Sax Polymers SAXAMID 226K6 Nylon 6.6, 30% Glass Beads SAXAMID 226K6 is a polyamide 6.6 injection-molding-grade filled with 30% glass beads. It is characterized by optimized shrinkage properties.Information provided by SAX Polymers |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 3.20 mm |
185 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Stat-kon AD000Z ABS LNP* Stat-Kon AD000Z is a compound based on ABS resin with carbon powder. Grade characteristics: a statically conductive extrusion grade.This data was supplied by SABIC-IP for the Americas region... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Xenoy® X3108UV PBT+PC (Asia Pacific) Unreinforced, UV-stabilized, flame retardant, impact modified PBT+PC with V0 at 0.8mm thickness. For interior and exterior applications like wall switches and electrical enclosures.This data was sup.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | 0.25 inch; ASTM D648 |
| PlastxWorld CEVIAN® B1700 PBT/ABS Alloy Unfilled, High Heat ResistantThese are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | DIN 53461 |
| Polyram PlusTek PA841 Nylon 6.6, Impact Modified Impact modified polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Tipco Tipcolene® FPT 30 BK CP - 30% Talc Polypropylene Homopolymer, Special Heat Stability 30% Talc Reinforced PP Homopolymer with Special AdditivesApplications: AutomotivesProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | Annealed; ASTM D648 |
| American Polymers API 505 Polystyrene API 505 is an intermediate grade of impact modified polystyrene. This material has exceptional moldability and colorability.Applications: API 505 is widely used in housewares, toys, containers, dis.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Eastman Tenite 285E0V16304 Cellulose Acetate Butyrate, Clear, Trsp Applications:DisplaysProduct Description: Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. T.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75-1/-2 |
| Covestro Bayblend® FR 3020 Polycarbonate + ABS, Mineral Filled 5 % mineral filledfor thin-wall applicationsinjection moldingVicat/B 120 = 103 °CHDT/A = 85 °Cvery good UL listing in small wall thickness (V-0 at 0.75 mm)PreprocessingMax. Water content |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75-1/-2 |
| Covestro Bayblend® FR 3021 Polycarbonate + ABS, Mineral Filled 15 % mineral filledinjection molding gradeincreased stiffnesstensile modulus = 4800 MPaVicat/B 120 temperature = 98 °CUL-listing 94 V-0 (1.5 mm) antimony-, chlorine- and bromine-free flame ret.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| E-Polymers TEKAMID® TB120CR Fast Crystallinity PA6 Resin Polyamide (Nylon) Resin. TEKAMID is widely being used in manufacturing of automotive and industrial parts with its outstanding mechanical, thermal and chemical properties.T-series: Impact modified,.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | unannealed; ISO 75 |
| Chi Mei Polylac® PA-758 ABS - Transparent Transparent |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75-2/AF |
| Addiplast Addinyl A2 E Flame Retardant Nylon 66 Flame retardant, halogen freeInformation provided by Addiplast. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Asahi Kasei Xyron® 140Z Modified Polyphenylene Ether Flame RetardantInformation provided by Asahi Kasei |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75-2 |
| BASF Ultraform® N2520 L POM Description: Is a POM, product having reduced electric surface resistance.Information provided by BASF |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 - 175 °C | 185 - 347 °F | Average value: 154 °C Grade Count:17 |
| Overview of materials for Polypropylene with 60% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 60% Glass Fiber Filler". Specific grades with glass content between 55% and 64% are i.. |
|||