Sax Polymers SAXAMID 226K6 Nylon 6.6, 30% Glass Beads
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Bead Filled |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 226K6 Nylon 6.6, 30% Glass Beads.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 226K6 is a polyamide 6.6 injection-molding-grade filled with 30% glass beads. It is characterized by optimized shrinkage properties.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 4.20 GPa | 609 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 153 MPa | 22200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.50 GPa | 508 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 3.00 kJ/m² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 18.0 kJ/m² @Temperature -30.0 °C |
8.57 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 28.0 kJ/m² @Temperature 23.0 °C |
13.3 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 1.70 J/cm² @Temperature -30.0 °C |
8.09 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 3.40 J/cm² @Temperature 23.0 °C |
16.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 235 °C | 455 °F | B/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- SGL Carbon Group EK 200 Graphite
- Special Metals NIMONIC® Alloy 80A
- Styron EMERGEâ„¢ 4630-10 Polycarbonate
- Master Bond EP45HTAO Heat Resistant Epoxy for Structural Bonding
- Eagle Brass 302 Austenitic Stainless Steel, 1/8 Hardened
- Covestro Makrolon® FR 7087 Polycarbonate
- Chosun Refractories HACT-170 High Alumina Castables
- BASF Sicotan® Brown K 2711 Color Additive
Copyright © lookpolymers.com All Rights Reserved