- Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded
- Chi Mei Polylac® PA-758 ABS - Transparent
Chi Mei Polylac® PA-758 ABS - Transparent
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polylac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polylac® PA-758 ABS - Transparent.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Transparent
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Melt Flow | 34 g/10 min @Load 10.0 kg, Temperature 220 °C |
34 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 90.0 MPa | 13100 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 33.0 MPa | 4790 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 50 % | 50 % | 50 mm/min; ISO 527 |
| Flexural Strength | 56.0 MPa | 8120 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.50 GPa | 218 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179 |
| Impact | 11.0 | 11.0 | Impact Flexural Test Notched (KJ/m²) |
| 60.0 | 60.0 | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | unannealed; ISO 75 |
| 96.0 °C | 205 °F | annealed; ISO 75 | |
| Vicat Softening Point | 98.0 °C @Load 5.00 kg |
208 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 101 °C @Load 5.00 kg |
214 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 104 °C @Load 1.00 kg |
219 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 106 °C @Load 1.00 kg |
223 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
Users viewing this material also viewed the following:
- Osprey Metals 304L Stainless Steel Powder (Grade 90% - 22)
- PolyOne Geon™ Vinyl Fittings 210(HR) Polyvinyl Chloride, Rigid (PVC, Rigid)
- PTS Tristar® PC-10FRNH-V 12 MFI Non-Bromine Non-Chlorine Flame Retardant UV Stabilized Polycarbonate With Release
- Huntsman AVALON® 90 AHT Thermoplastic Polyurethane
- Shinkong Synthetic Fibers Shinite® T101G36 PET, 36% Glass Filled
- Clariant Renol PA211 Nylon 6, General Purpose
- Americas Styrenics STYRON® 665 High Heat Crystal Polystyrene
- Plastcom SLOVALEN PC 91 T 30 PP, 30% mineral filling
- Von Roll Isola IMI Varnish 702 Solventless Polyester Varnish for Electrical Insulation
Copyright © lookpolymers.com All Rights Reserved