SABIC Innovative Plastics LNP Verton NV0061EV_GY7E148 PC+ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP VERTON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Verton NV0061EV_GY7E148 PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Preliminary data for 30% long fiber single pellet non-halogen FR color filled PC/ABSThis data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
ISO 1183
1.453 g/cc
0.05249 lb/in³
ASTM D 792
Water Absorption 0.090 %

@Temperature 23.0 °C,
Time 86400 sec
 0.090 %

@Temperature 73.4 °F,
Time 24.0 hour
 ISO 62-1
0.088 %

@Time 86400 sec
 0.088 %

@Time 24.0 hour
 ASTM D 570
Linear Mold Shrinkage, Flow 0.00080 - 0.0028 cm/cm

@Time 86400 sec
 0.00080 - 0.0028 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.0034 - 0.0054 cm/cm

@Time 86400 sec
 0.0034 - 0.0054 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 94.0 MPa
13600 psi
5 mm/min; ISO 527
112 MPa
16200 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 94.0 MPa
13600 psi
5 mm/min; ISO 527
112 MPa
16200 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 1.1 %
1.1 %
5 mm/min; ISO 527
1.3 %
1.3 %
Type I, 5 mm/min; ASTM D 638
1.6 %
1.6 %
Flexural Strain, 2 mm/min; ISO 178
Elongation at Yield 1.1 %
1.1 %
5 mm/min; ISO 527
1.3 %
1.3 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 9.06 GPa
1310 ksi
1 mm/min; ISO 527
9.76 GPa
1420 ksi
50 mm/min; ASTM D 638
Flexural Strength 142 MPa
20600 psi
1.3 mm/min, 50 mm span; ASTM D 790
143 MPa
20700 psi
2 mm/min; ISO 178
Flexural Yield Strength 142 MPa
20600 psi
1.3 mm/min, 50 mm span; ASTM D 790
143 MPa
20700 psi
2 mm/min; ISO 178
Flexural Modulus 8.91 GPa
1290 ksi
2 mm/min; ISO 178
10.2 GPa
1480 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 1.84 J/cm

@Temperature -40.0 °C
 3.45 ft-lb/in

@Temperature -40.0 °F
 ASTM D 256
2.38 J/cm

@Temperature 23.0 °C
 4.46 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 3.29 J/cm

@Temperature 23.0 °C
 6.16 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
3.74 J/cm

@Temperature -40.0 °C
 7.01 ft-lb/in

@Temperature -40.0 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 21.0 kJ/m²

@Temperature 23.0 °C
 9.99 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
21.0 kJ/m²

@Temperature -40.0 °C
 9.99 ft-lb/in²

@Temperature -40.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 26.0 kJ/m²

@Temperature -40.0 °C
 12.4 ft-lb/in²

@Temperature -40.0 °F
 80*10*4; ISO 180/1U
27.0 kJ/m²

@Temperature 23.0 °C
 12.8 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 10.0 J

@Temperature 23.0 °C
 7.38 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 27.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 15.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 66.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 37.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C
189 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
85.0 °C

@Thickness 3.20 mm
 185 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Flammability, UL94 V-0

@Thickness 1.50 - 1.60 mm
 V-0

@Thickness 0.0591 - 0.0630 in
 UL 94