Covestro Bayblend® FR 3020 Polycarbonate + ABS, Mineral Filled

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	Covestro
Trade Name	Bayblend®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Covestro Bayblend® FR 3020 Polycarbonate + ABS, Mineral Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

5 % mineral filledfor thin-wall applicationsinjection moldingVicat/B 120 = 103 °CHDT/A = 85 °Cvery good UL listing in small wall thickness (V-0 at 0.75 mm)PreprocessingMax. Water content

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/in³	ISO 1183
Water Absorption	0.50 %	0.50 %	Similar to ISO 62
Moisture Absorption at Equilibrium	0.20 %	0.20 %	Similar to ISO 62
Melt Flow	24 g/10 min @Load 5.00 kg, Temperature 240 °C	24 g/10 min @Load 11.0 lb, Temperature 464 °F	estimated from MVR using room temperature density; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	65.0 MPa	9430 psi	ISO 527-1/-2
Elongation at Yield	4.0 %	4.0 %	ISO 527-1/-2
Tensile Modulus	3.20 GPa	464 ksi	ISO 527-1/-2

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	85.0 °C	185 °F	ISO 75-1/-2
Vicat Softening Point	101 °C	214 °F	50°C/h 50N; ISO 306
Flammability, UL94	V-0 @Thickness 0.800 mm	V-0 @Thickness 0.0315 in	IEC 60695-11-10
	5VB @Thickness 2.00 mm	5VB @Thickness 0.0787 in	IEC 60695-11-20

Processing Properties	Metric	English	Comments
Melt Temperature	240 °C	464 °F	Injection Molding; ISO 294
	240 - 270 °C	464 - 518 °F
Mold Temperature	60.0 - 80.0 °C	140 - 176 °F
	80.0 °C	176 °F	Injection Molding; ISO 10724
Injection Velocity	240 mm/sec	9.45 in/sec	ISO 294

Descriptive Properties	Value	Comments
Availability	Asia Pacific
	Europe
	India
	Near East/Africa
	South and Central America
Feature	Release agent
Form	Pellets
Process	Injection Molding