SABIC Innovative Plastics Xenoy® CL402 PBT+PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® CL402 PBT+PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
XENOY CL402 is a high viscosity, unfilled, elastomer modified PC/PBT blend for extrusion/blowmolding applications. ISO1043-label: PC+PBT-I.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.50 % @Temperature 23.0 °C |
0.50 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.012 cm/cm @Thickness 3.20 mm |
0.0090 - 0.012 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 250 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D 1238 |
| 6.0 g/10 min @Load 5.00 kg, Temperature 250 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 482 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 85.0 MPa | 12300 psi | ISO 2039-1 |
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D 638 |
| 41.0 MPa | 5950 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | Type I, 50 mm/min; ASTM D 638 |
| 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 50 % | 50 % | Type I, 50 mm/min; ASTM D 638 |
| 50 % | 50 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 4.5 % | 4.5 % | Type I, 50 mm/min; ASTM D 638 |
| 4.5 % | 4.5 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 1.90 GPa | 276 ksi | 50 mm/min; ASTM D 638 |
| 1.90 GPa | 276 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 65.0 MPa | 9430 psi | 2 mm/min; ISO 178 |
| 70.0 MPa | 10200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 1.90 GPa | 276 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 1.90 GPa | 276 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 3.50 J/cm @Temperature -30.0 °C |
6.56 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 4.75 J/cm @Temperature 0.000 °C |
8.90 ft-lb/in @Temperature 32.0 °F |
ASTM D 256 | |
| 5.75 J/cm @Temperature 23.0 °C |
10.8 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 30.0 kJ/m² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 50.0 kJ/m² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| Charpy Impact, Notched | 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Impact Test | 50.0 J @Temperature 23.0 °C |
36.9 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Taber Abrasion, mg/1000 Cycles | 40 @Load 1.00 kg |
40 @Load 2.20 lb |
CS-17; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 105 µm/m-°C @Temperature -40.0 - 40.0 °C |
58.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 110 µm/m-°C @Temperature 23.0 - 80.0 °C |
61.1 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 105 µm/m-°C @Temperature -40.0 - 40.0 °C |
58.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 110 µm/m-°C @Temperature 23.0 - 80.0 °C |
61.1 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 85.0 °C @Thickness 3.20 mm |
185 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 123 °C | 253 °F | Rate B/50; ASTM D 1525 |
| 123 °C | 253 °F | Rate B/50; ISO 306 | |
| 125 °C | 257 °F | Rate B/120; ISO 306 | |
| 155 °C | 311 °F | Rate A/50; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.3 @Frequency 50.0 - 60.0 Hz |
3.3 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 17.0 kV/mm @Thickness 3.20 mm |
432 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 18.0 kV/mm @Thickness 1.60 mm |
457 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0020 @Frequency 50.0 - 60.0 Hz |
0.0020 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Pau Tai UNISTAB RP-33K Solid Complex Stabilizer
- Gichem GIBLEND F70500 Polycarbonate / ABS (discontinued **)
- Overview of materials for Polycarbonate, Aramid Fiber Reinforced
- LyondellBasell Petrothene® NA336149 Low Density Polyethylene
- LG Chemical LUPOL GP3300 PP+MF30%
- SABIC Innovative Plastics LNP THERMOCOMP Noryl_FM3020 PPE+HIPS (Europe-Africa-Middle East)
- Addiplast Addilene H 555 Y7 Polypropylene Homopolymer
- BASF Ultramid® S3K Balance PA 610 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved