SABIC Innovative Plastics LNP THERMOCOMP KZ002 Acetal
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP KZ002 Acetal.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* KZ002 is a compound based on Acetal containing 10% Milled Glass.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ASTM D792 |
| 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.180 % | 0.180 % | 50% RH, 24 hrs; ASTM D570 |
| 0.260 % | 0.260 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | Type I, 5 mm/min; ASTM D638 |
| 54.0 MPa | 7830 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | Type I, 5 mm/min; ASTM D638 |
| 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 18.6 % | 18.6 % | Type I, 5 mm/min; ASTM D638 |
| 21.3 % | 21.3 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 9.6 % | 9.6 % | Type I, 5 mm/min; ASTM D638 |
| 10.1 % | 10.1 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.41 GPa | 495 ksi | 1 mm/min; ISO 527 |
| 3.63 GPa | 526 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 74.0 MPa | 10700 psi | ISO 178 |
| Flexural Modulus | 2.77 GPa | 402 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.95 GPa | 428 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.16 J/cm | 15.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 49.0 kJ/m² | 23.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 110 µm/m-°C @Temperature -30.0 - 30.0 °C |
61.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 106 µm/m-°C @Temperature -30.0 - 30.0 °C |
58.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C @Thickness 3.20 mm |
307 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 153 °C | 307 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 101 °C @Thickness 3.20 mm |
214 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 103 °C @Thickness 3.20 mm |
217 °F @Thickness 0.126 in |
annealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nylene® PX3422 Nylon 6, Impact Extrusion Grade
- Premix Premi-Glas® 3101-10 Fiberglass Reinforced Thermoset BMC
- NOVA Chemicals Surpass® FPs225-A Octene Copolymer sLLDPE Film Resin
- SABIC Innovative Plastics LNP COLORCOMP PX99848 PA 6
- LG Chemical LS080S PVC
- Borealis Nepol™ GB601HP Polypropylene, 40% Long Glass Fiber Reinforced w/HK060AE
- Carlisle 201HL Carbon-Carbon Composite
- Akro-Plastic Akromid® B3 GF 10 (2829) PA 6 Conditioned, 10% Glass Filled
- 3M Scotchcal™ 8671 Perforated Window Graphic Film
- Bhansali Engineering Abstron IMGS20 Glass Reinforced Grade
Copyright © lookpolymers.com All Rights Reserved