Aclo Accutech Polypropylene Copolymer CP0437G25M5CL Glass/Mineral Reinforced Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Glass/Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0437G25M5CL Glass/Mineral Reinforced Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | MD; ASTM D955 |
| Melt Flow | 9.0 g/10 min | 9.0 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 75 | 75 | ASTM D785 |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | ASTM D638 |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | ASTM D638 |
| Elongation at Break | 9.0 % | 9.0 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 3.20 GPa | 464 ksi | ASTM D638 |
| Flexural Strength | 60.0 MPa | 8700 psi | ASTM D790 |
| Flexural Modulus | 3.499 GPa | 507.5 ksi | ASTM D790 |
| Izod Impact, Notched | 1.66 J/cm | 3.10 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F |
Users viewing this material also viewed the following:
- PolyOne Synprene™ RT-5190 RoHS Black Styrene Butadiene Block Copolymer (SBC)
- Quantum Composites QC-3450 48% Glass Fiber High Temperature Use SMC (discontinued **)
- Kolon KOPA® KN333G33CR G/F Reinforced Nylon 66
- Struktol POLYDIS 3610 Reactive, elastomer modified epoxy prepolymer (block-copolymer)
- Silikony Polskie Polsil E2 Silicone Emulsion
- Teknor Apex Synres® SR 1288A Polypropylene
- Goodfellow Nickel 80/Molybdenum 20 Alloy
- Axiall 22851 Coax & Telecom Flexible PVC
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR Mistron Vapor Filler
- LATI LARAMID CE/60 60% Mineral Filled Polyphthalamide (PPA) Based Compound (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved