- Polyram RamOfin PPH300G6 Polypropylene, 30% Glass Fiber
Polyram RamOfin PPH300G6 Polypropylene, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamOfin PPH300G6 Polypropylene, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass fiber reinforced polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | DIN 53479 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 230 °C |
14 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM-D785 |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM-D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM-D638 |
| Flexural Strength | 105 MPa | 15200 psi | ASTM D790 |
| Flexural Modulus | 5.70 GPa | 827 ksi | ASTM-D790 |
| Izod Impact, Notched | 1.05 J/cm @Temperature 23.0 °C |
1.97 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous Use |
| 140 °C | 284 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
Users viewing this material also viewed the following:
- Mytex Polymers AS20LW Polypropylene, Talc filled, Compounded
- Nilit FRIANYL A63 TF-GV 1530 Nylon 6.6 for injection molding, 15% PTFE lubricated and 30% glass fiber reinforced
- LG Chemical Lupox® GP2306FI PBT+GF30%
- SABIC Innovative Plastics ULTEM AR9300 PEI
- Stir SpA SG 70 K8 (PVC)
- SABIC Innovative Plastics LNP Thermocomp ZWM2411 PPE+PS (Asia Pacific)
- Teknor Apex Telcar® TL-2596C Thermoplastic Elastomer
- Eastman Tritan TX1501HF Copolyester
- Aclo Accutech Polyethylene HD0234G20UVL High Density Glass Reinforced UV Stabilized
- Arkema Group KYNAR FLEX® 2800-01 Polyvinylidene Fluoride Copolymer - Extrusion
Copyright © lookpolymers.com All Rights Reserved