SABIC Innovative Plastics LNP THERMOCOMP MX89510 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MX89510 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* MX89510 is a compound based on Polypropylene resin containing Proprietary Filler(s).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.02 g/cc | 1.02 g/cc | ASTM D792 |
| Density | 1.01 g/cc | 0.0365 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.020 cm/cm @Time 86400 sec |
0.0080 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.030 cm/cm @Time 86400 sec |
0.0090 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.0 MPa | 6960 psi | 5 mm/min; ISO 527 |
| 52.0 MPa | 7540 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 |
| 52.0 MPa | 7540 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 3.4 % | 3.4 % | Type I, 5 mm/min; ASTM D638 |
| 3.4 % | 3.4 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.9 % | 2.9 % | 5 mm/min; ISO 527 |
| 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 3.54 GPa | 513 ksi | 1 mm/min; ISO 527 |
| 3.82 GPa | 554 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 76.0 MPa | 11000 psi | ISO 178 |
| Flexural Yield Strength | 80.0 MPa | 11600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.80 GPa | 406 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.95 GPa | 428 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.210 J/cm | 0.393 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.68 J/cm | 6.89 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 43.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
23.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 120 µm/m-°C @Temperature -30.0 - 30.0 °C |
66.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 119 °C | 246 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 131 °C @Thickness 3.20 mm |
268 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Ovation Polymers Opnyl OP66GF43 Nylon 66, As Conditioned
- Huntsman HT 939 Special Hardener
- Lucent Polymers PC-1428 Polycarbonate, Injection Grade
- Lehmann & Voss LUVOCOM® 1-0866 Polyamide 66, with aramid reinforcement, heat stabilized
- A. Schulman POLYFORT™ FPP 1602 Glass Reinforced, Chemically Coupled Homopolymer
- Wieland Porta SMK 82 PFM Alloy
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 2.0 PHR MBTS
- Dow Corning HMW 2220 Non-Ionic Emulsion
- Eurotec® Tecodur® PB70 NL XA20 PBT, flame retardant - halogen (RoHS compliant), heat stabilized, natural
- 3M Nextel™ AP-18 Woven Tape 312 (3.8 cm)
Copyright © lookpolymers.com All Rights Reserved