- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 437 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 437 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C @Thickness 3.18 mm |
437 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Nymax™ GB 1200 30 HS BLACK 18 Polyamide 66 (Nylon 66) Preliminary Data SheetMolded Test Bars: Dry as MoldedInformation provided by PolyOne |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ASTM D648 |
| Nilit Polynil® N66-P300 High Viscosity Nylon 6/6 Information provided by US distributor Polymer Technology and Services, LLC (PTS). |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ASTM D648 |
| Nilit Polynil® P36 Very High Flow Nylon 66 Description: Very high flowApplication: CompoundingInformation provided by NILIT. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ISO 75-1/-2 |
| DSM Arnite® CCT GF30 (T-X01301) PBT-30% Glass Reinforced (European Grade)
(discontinued **) Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.Arnite Molding resins: Standard Unfilled and Reinforced materialsHigh modulus Flame .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ISO 75-1/-2 |
| Lanxess Pocan® T 7391 POS151 000000 PBT + PET, 45% Glass Fiber
(discontinued **) PBT+PET, 45% glass fibers, injection molding, improved surface finish, increased temperature peak load, UV-stabilized |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 - 255 °C | 437 - 491 °F | Average value: 245 °C Grade Count:6 |
| Overview of materials for Nylon 66/Nylon 6 Blend, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/Nylon 6 Blend, Glass Fiber Filled". Each property range of values reported is minimum and maxim.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C @Thickness 6.40 mm |
437 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUMID HI1102B(W) PA66, High Impact Feature: Injection Molding,PA66, High ImpactApplication: Automotive (Covers)CAS No. 32131-17-2 and 9010-79-1Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | |
| LATI Latamid 6 H2 G/55 PA 6, 55% Glass Fiber Reinforced, Heat Stabilized Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termopla.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ISO 75-1/-2 |
| Lanxess Durethan® A 30 000000 Nylon 66 PA 66, standard injection molding grade, non-reinforced, very easy release, normal solidificationApplication Examples: terminal blocks, cable clips, bobbins, gearwheels |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | |
| LATI Later 4 G/50 PBT, 50% Glass Fiber Reinforced Polybutylene Terephthalate (PBT) based compound. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplast.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics Valox® ENH4560 PBT (Europe-Africa-Middle East) Valox* ENH4560 resin is a non-brominated/non-chlorinated flame retardant product based on Valox* PBT resin. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP JF004Z PES (Europe-Africa-Middle East) LNP* Thermocomp* JF004Z is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: HV. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C @Thickness 6.40 mm |
437 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® GP-5300G PBT, Glass Filled Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ASTM D648 |
| Samyang Tribit® 1500G15 Polybutylene Terephthalate, 15% Glass Reinforced Characteristics:G/F reinforcedHeat and Impact resistantApplications:AutomotiveConnectorGearOutdoor handleIgnition systemElectronicConnectorGas valveCoil bobbinSwitch caseRelay caseO/A partsAll infor.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Valox® 430 PBT (Europe-Africa-Middle East) VALOX 430 is 33% glass reinforced, impact modified PBT injection moulding resin. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ISO 75 |
| Polyram PlusTek PA803 Nylon 6.6 for Injection Molding, Impact Modified Impact modified Nylon 6.6 for injection molding application.Information provided by Polyram. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ASTM D648 |
| Cheng Yu Plastic T883GV2 Flame Retardant PBT, 20% Glass Fiber |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ASTM D648 |
| Cheng Yu Plastic T889G2 PBT, 20% Glass Fiber |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® AS/2 PA66 Product description: Grilon AS/2 is an unreinforced PA66 injection molding grade. Grilon AS/2 has the following important properties: Good flow behaviorEasy processingShort cycle times Grilon AS/2 i.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ISO 75-1/2 |
| Eurotec® Tecomid® NA40 NL FA 50 PA 6.6 unreinforced, UL94 V0, halogen/phosphorus free Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Eurostar Staramide RB008 PA66, 40% Glass Bead Filled, Injection Molded Staramide RB008 is a 40% Glass Bead Reinforced Polyamide 66 Injection Molding ResinInformation provided by Eurostar. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ASTM D648 |
| Clariant Renol PA121 Nylon 66, Impact Modified Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ISO 75-2 |
| BASF Ultradur® B 4406 G6 30% Glass Filled PBT Description: Is a PBT, flame-retardant injection-molding grades, with 30% glass fibers, for parts requiring enhanced fire resistance, e.g. plug-and-socket connectors, housings, coil formers and ligh.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ISO 75-1/-2 |
| DSM Arnite® TV4 261 KL PBT-GF30 30% Glass Reinforced, Light Stabilized |
|||