Nilit Polynil® N66-P300 High Viscosity Nylon 6/6
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Nilit |
| Trade Name | Polynil® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit Polynil® N66-P300 High Viscosity Nylon 6/6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 80.0 MPa @Thickness 3.17 mm |
11600 psi @Thickness 0.125 in |
|
| Elongation at Break | 52 % @Thickness 3.17 mm |
52 % @Thickness 0.125 in |
|
| Izod Impact, Notched | 0.800 J/cm @Thickness 3.17 mm |
1.50 ft-lb/in @Thickness 0.125 in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 258 °C | 496 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 254 °C | 490 °F | |
| Middle Barrel Temperature | 268 °C | 515 °F | |
| Front Barrel Temperature | 285 °C | 545 °F | |
| Nozzle Temperature | 266 - 282 °C | 510 - 540 °F | |
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 26.7 - 93.3 °C | 80.0 - 200 °F | |
| Drying Temperature | 71.1 °C | 160 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 68.9 MPa | 10000 psi | |
| Back Pressure | 0.0689 - 0.689 MPa | 10.0 - 100 psi | |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm |
Users viewing this material also viewed the following:
- ExxonMobil Escorene® LL-5102 LLDPE Compounding Resin (discontinued **)
- Chevron Phillips Ryton® R-7-220NA Polyphenylene Sulfide Resin (discontinued **)
- Overview of materials for Nylon 12, Glass Bead Filled
- Lanxess Durethan® BKV 230 H2.0 901510 Copolyamide, 30% Glass Fiber
- SABIC Innovative Plastics LNP LUBRICOMP RX99518 PA 66
- ExxonMobil QQ Mobiltac Double Letter Series
- Dow Corning 7-3123 MANGO BLEND EMULSION
- Fiberfil® J-62/30/E Polypropylene Copolymer, 30% Glass Fiber Reinforced, Chemically coupled
Copyright © lookpolymers.com All Rights Reserved