Lanxess Pocan® T 7391 POS151 000000 PBT + PET, 45% Glass Fiber  (discontinued **)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Pocan® T 7391 POS151 000000 PBT + PET, 45% Glass Fiber  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT+PET, 45% glass fibers, injection molding, improved surface finish, increased temperature peak load, UV-stabilized
Physical Properties Metric English Comments
Density 1.68 g/cc
0.0607 lb/in³
ISO 1183
Water Absorption 0.30 %
0.30 %
Test Sim. to ISO 62
Moisture Absorption at Equilibrium 0.10 %
0.10 %
23°C/50% R.H.; Test Sim. to ISO 62
Viscosity Test 80 cm³/g
80 cm³/g
Viscosity number; ISO 307, 1157, 1628
Melt Flow 42 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 42 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 Calculated from MVR using melt density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 165 MPa
23900 psi
ISO 527-1/-2
Elongation at Break 2.0 %
2.0 %
ISO 527-1/-2
Tensile Modulus 16.5 GPa
2390 ksi
ISO 527-1/-2
Charpy Impact Unnotched 7.00 J/cm²

@Temperature -30.0 °C
 33.3 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
7.00 J/cm²

@Temperature 23.0 °C
 33.3 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 1.10 J/cm²

@Temperature -30.0 °C
 5.23 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
1.20 J/cm²

@Temperature 23.0 °C
 5.71 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Tensile Creep Modulus, 1 hour 16500 MPa
2.39e+6 psi
ISO 899-1
Tensile Creep Modulus, 1000 hours 15000 MPa
2.18e+6 psi
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C
11.1 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 50.0 µm/m-°C
27.8 µin/in-°F
ISO 11359-1/-2
Melting Point 225 - 250 °C
437 - 482 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 225 °C
437 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 150 °C
302 °F
ISO 75-1/-2
Vicat Softening Point 210 °C
410 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
 IEC 60695-11-10
HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
 IEC 60695-11-10
Oxygen Index 21 %
21 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 4.2

@Frequency 1.00e+6 Hz
 4.2

@Frequency 1.00e+6 Hz
 IEC 60250
4.3

@Frequency 100 Hz
 4.3

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 28.0 kV/mm
711 kV/in
IEC 60243-1
Dissipation Factor 0.0020

@Frequency 100 Hz
 0.0020

@Frequency 100 Hz
 IEC 60250
0.014

@Frequency 1.00e+6 Hz
 0.014

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 275 V
275 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 270 °C
518 °F
Injection Molding; ISO 294
Mold Temperature 90.0 °C
194 °F
Injection Molding; ISO 10724
Descriptive Properties Value Comments
Additives Release agent
Features U.V. stabilized or stable to weather
Form Pellets
ISO Shortname ISO 7792-1-PBT+PET,GHLMR,09-160,GF45
Processing Injection molding
Region Asia Pacific
Europe
Near East/Africa
North America
South and Central America