Samyang Tribit® 1500G15 Polybutylene Terephthalate, 15% Glass Reinforced
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | Samyang |
| Trade Name | Tribit® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Tribit® 1500G15 Polybutylene Terephthalate, 15% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics:G/F reinforcedHeat and Impact resistantApplications:AutomotiveConnectorGearOutdoor handleIgnition systemElectronicConnectorGas valveCoil bobbinSwitch caseRelay caseO/A partsAll information provided by Samyang
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 |
| Water Absorption | 0.080 % @Time 86400 sec |
0.080 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.012 cm/cm @Thickness 3.00 mm |
0.0020 - 0.012 in/in @Thickness 0.118 in |
ASTM D955 |
| Melt Flow | 50 g/10 min @Load 5.00 kg, Temperature 250 °C |
50 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Yield | 98.1 MPa | 14200 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Flexural Yield Strength | 157 MPa | 22800 psi | ASTM D790 |
| Flexural Modulus | 5.88 GPa | 853 ksi | ASTM D790 |
| Izod Impact, Unnotched | 0.588 J/cm @Thickness 3.17 mm |
1.10 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ASTM D696 |
| Melting Point | 226 °C | 439 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 21.0 kV/mm | 533 kV/in | ASTM D149 |
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 150 sec | 150 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |
| Middle Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |
| Front Barrel Temperature | 220 - 230 °C | 428 - 446 °F | |
| Nozzle Temperature | 250 - 270 °C | 482 - 518 °F | |
| Melt Temperature | 265 °C | 509 °F | |
| Drying Temperature | 110 - 130 °C | 230 - 266 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | |
| Moisture Content | 0.010 - 0.015 % | 0.010 - 0.015 % | |
| Screw Speed | 60 - 80 rpm | 60 - 80 rpm |
Users viewing this material also viewed the following:
- Resinoid 2225 Phenolic Molding, Cellulose Reinforced
- LyondellBasell Pro-fax 6301 Polypropylene Homopolymer, Flake Resin
- Saint-Gobain CHR® SG06-10(R) Premium Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- SABIC Innovative Plastics Xylex X7529OQ PC+POLYESTER (Europe-Africa-Middle East)
- Chevron Phillips Marlex® HXM 50100 Extra high molecular weight hexene copolymer
- ExxonMobil LDPE LD 159AC Low Density Polyethylene Resin
- Dow TUFLIN™ HS-7094 NT 7 Linear Low Density Polyethylene Resin
- Fainplast Compounds PK 91 Flexible PVC, Lead Free
- Huntsman Rexell® L8404 Cast Film Extrusion LLDPE (discontinued **)
- A. Schulman POLYPUR™ FPU 1380 Thermoplastic Polyurethane Compound
Copyright © lookpolymers.com All Rights Reserved