PolyOne Nymax™ GB 1200 30 HS BLACK 18 Polyamide 66 (Nylon 66)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer PolyOne Corporation
Trade Name Nymax™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Nymax™ GB 1200 30 HS BLACK 18 Polyamide 66 (Nylon 66).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Preliminary Data SheetMolded Test Bars: Dry as MoldedInformation provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.38 g/cc
1.38 g/cc
ASTM D792
Water Absorption 0.90 %

@Thickness 0.318 mm
 0.90 %

@Thickness 0.0125 in
 @ 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.014 cm/cm
0.014 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.8 MPa
7800 psi
Type I, 5.1 mm/min; ASTM D638
Elongation at Break 2.0 %
2.0 %
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 110 MPa
16000 psi
ASTM D790
Flexural Modulus 3.72 GPa
540 ksi
ASTM D790
Izod Impact, Notched 0.350 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
 0.656 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
 Injection Molded; ASTM D256A
Thermal Properties Metric English Comments
Melting Point 265 °C
509 °F
ASTM D789
Deflection Temperature at 0.46 MPa (66 psi) 225 °C

@Thickness 3.18 mm
 437 °F

@Thickness 0.125 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C

@Thickness 3.18 mm
 176 °F

@Thickness 0.125 in
 Unannealed; ASTM D648
Processing Properties Metric English Comments
Mold Temperature 60.0 - 107 °C
140 - 225 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Filler / Reinforcement Glass Bead
Unspecified FillerReinfor., 30% Filler by Weight
Forms Pellets
Generic Material Nylon 66
Generic Name Polyamide 66 (Nylon 66)
Regional Availability North America
South America