Eurostar Staramide RB008 PA66, 40% Glass Bead Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Bead Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide RB008 PA66, 40% Glass Bead Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide RB008 is a 40% Glass Bead Reinforced Polyamide 66 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm @Thickness 4.00 mm |
0.014 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 83.0 MPa | 12000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 5.20 GPa | 754 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 128 MPa | 18600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.40 GPa | 638 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80x10x4; ISO 179/1eA |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 58.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
32.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 57.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
31.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 260 - 280 °C | 500 - 536 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 270 - 290 °C | 518 - 554 °F | |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL4016H PC Copolymer (Europe-Africa-Middle East)
- Hannam Chemical Hanalac 795 ABS, Pipe Grade
- Lavergne VYTEEN PC/ABS 8515 Polycarbonate - Acrylonitrile Butadiene Styrene Alloy
- Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure
- SABIC Innovative Plastics ULTEM ATX200F PEI+PCE (Asia Pacific)
- SABIC Innovative Plastics Valox® 325 PBT (Europe-Africa-Middle East)
- Master Bond EP21TDC-4ND Two component, highly flexibilized epoxy for bonding, sealing and coating
- Dow Corning SILASTIC® MDX4-4210 BIOMEDICAL GRADE ELASTOMER WITH CATALYST
- Solvay Specialty Polymers Algoflon® 35CAR PTFE; Petroleum Coke and Graphite (discontinued **)
- Eurostar Star L PA66 15Y D52 PA66, Carbon Filled, Injection Molded
Copyright © lookpolymers.com All Rights Reserved