- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 98.0 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 98.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C @Thickness 3.18 mm |
208 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Maxxam™ FR PP FR 7B01 Polypropylene, Unspecified (PP, Unspecified) Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C @Thickness 3.20 mm |
208 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Cycolac® MG37CR ABS (Asia Pacific) High performance, injection molding ABS. Overall balance of physical properties, good processability and chemical resistance.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYasa 1614F UV-resistant ASA Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C @Thickness 6.40 mm |
208 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® C6600 PC+ABS Nonbrominated, nonchlorinated FR PC+ABS with balanced flow, impact and hydrolytic stability for a wide variety of applications including business equipment, monitors, enclosures, among others. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics Cycoloy® CY6110 PC+ABS Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow / impact balance for a wide variety of thin wall or la.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics Geloy XTWM206 ASA Next generation ASA optimized for outstanding weatherability, colorability and higher heat applications requiring UV exposure resistance.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP FARADEX AS004 ABS (Europe-Africa-Middle East) LNP* Faradex* AS004 is a compound based on Acrylonitrile Butadiene Styrene resin containing Stainless Steel Fiber. Added features of this material include: EMI/RFI Shielding. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | ISO 75 |
| Phillips Sumika Marlex® CHP-275 Thermoplastic Polyolefin
(discontinued **) Engineered Thermoplastic Polyolefin.Applications: Automotive Head and Side Impact TrimConditioning after Molding: 48 hr at 23°C, 48 hr at 90°CNominal Shrinkage: 0.7-0.9%, 0.8-1.1%Drying conditions.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | |
| Polycasa Acryl® KR 2008/1 Acrylic, Impact Grade Impact grade for extruded tubes and profiles; e.g. strip light diffusers; good scratch and abrasion resistance.Data was collected by ISO methods.Quinn Manufacturing Group rebranded its Plastics Divi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | ASTM D648 |
| Reliance Industries Repol H080EG Polypropylene REPOL Polypropylene H080EG is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific cataly.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | Annealed, 80°C, 4 hours; ISO 75 |
| LG Chemical AF-348 ABS, Flame Retardant, Heat Resistant, Weather Resistant Information Provided by LG Chem |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | ISO 75-1,-2 |
| Ineos ABS Lustran® M205FC ABS Pellets, Injection Molding Grade Injection Molding grade for medical applications (e.g. inhalers, roller clamps, spikes, etc.)/ Biocompatible with up to 30 days human contact duration according to USP Class VI and ISO 10993-1. Food.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | |
| Ineos ABS Lustran® M305 Grade for smart cards, good dimensional accuracy, excellent dynamic loading capacity.,Property data per ISO test methods. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 2-3110 TO BU 10% Talc Filled Polypropylene Copolymer INNOPOL® CS 2-3110 TO BU is a 10% talc-filled, black colored and UV stabilized compound based on polypropylene block-copolymer.INNOPOL® CS 2-3110 TO BU is developed for producing injection mol.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | Annealed, 80°C, 4 hours; ISO 75 |
| LG Chemical SH-610 ABS, Extrusion, High Impact Information Provided by LG Chem |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | ASTM D648 |
| IRPC Polimaxx Polene 2300SC Polypropylene Block Copolymer CHARACTERISTICS: HIGH FLOW, GOOD IMPACTAPPLICATIONS: INJECTION MOLDING FOR AUTOPARTS, ELECTRICAL APPLIANCES, THIN WALL PARTS |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | ASTM D648 |
| IRPC Polimaxx Polene 2363LC Polypropylene Block Copolymer CHARACTERISTICS: CONTAIN UV STABILIZER ADDITIVE, HIGH IMPACTAPPLICATIONS: INJECTION MOLDING FOR AUTOPARTS, ELECTRICAL APPLIANCES, FURNITURES, CRATES |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C @Thickness 6.40 mm |
208 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOY GN5001RFJ PC/ABS, Halogen Free Flame Retardant Description: Injection Molding, PC/ABS, Halogen Free Flame Retardant, High FlowApplication: IT/OA (OA Housing)CAS: 103598-77-2, 9003-56-9 and 181028-79-5Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C @Thickness 3.20 mm |
208 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON Lexan_JK2500 PC+ABS LNP* Stat-kon* Lexan_JK2500 compound is a 20% carbon-fiber reinforced, nonhalogenated red phosporous-free, high-flow FR PC+ABS for EMI/RFI shielding. SE of 21 dB at 1.5 mm. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | ISO 75 |
| Styrolution Novodur® M210TF ABS Novodur M210TF is medium impact, high gloss injection molding grade designed for toy application. M210TF is in compliance with food contact regulationsInformation provided by Styrolution |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | ISO 75-1,-2 |
| Styrolution Novodur® P2M-V ABS Pellets Novodur® P2M-V has high impact strength, high gloss, and low emission. It is used for the production of molded plastic articles. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | ISO 75-1/-2 |
| Styrolution Polystyrol 168 N GR 2 PS Description: Polystyrol 168 N is a high molecular, heat grade used where high strength is required. Suitable for physically or chemically expanded extruded sheet. As blend component with high impact.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C @Thickness 6.40 mm |
208 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® LX-0987EXS ABS, Unreinforced Metallic-Look Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C @Thickness 3.20 mm |
208 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP AH0400A ABS LNP* THERMOCOMP* AH0400A is a compound based on ABS resin. Added feature of this material is: High Specific Gravity. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | ASTM D648 |
| Tipco Tipcolene® X 408 IN - 10% Talc/Mineral Reinforced Polypropylene Copolymer, Very High Impact Strength & Flow 10% Mineral Reinforced, Very High Impact PP CopolymerApplications: Automotive BumpersProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | ASTM D648 |
| Braskem H 503 Raffia Extrusion & Fiber Extrusion Polypropylene Homopolymer ApplicationsRaffia Extrusion: Industrial bags; Flexible containers; Curtains and covers to aviary and agriculture.Fiber Extrusion: Monofilament for ropes; Fishing nets; Cables and ropes for boats; .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | ASTM D648 |
| Buckeye Polymers BP RPP 2011 C Polypropylene, 20% Mineral Filled Applications:Outdoor FurnitureCalcium carbonate-filled PP grades have a high impact toughness, moderate increased stiffness, and excel in high gloss applications. This material can be customized thr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | |
| BASF Polystyrol® 168 N Polystyrene (Europe) High molecular, heat-resistant grades used where high strength is required. Suitable for expanded film.Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | ASTM D648 |
| Braskem H 103 Extrusion Coating Polypropylene Homopolymer Description: H 103 is a high melt flow rate additivated homopolymer used for general purposes. The product exhibits excellent processing performance on injection moulding applications. Applications:.. |
|||