SABIC Innovative Plastics LNP STAT-KON Lexan_JK2500 PC+ABS

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Carbon Fiber Filled , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP STAT-KON
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP STAT-KON Lexan_JK2500 PC+ABS.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Stat-kon* Lexan_JK2500 compound is a 20% carbon-fiber reinforced, nonhalogenated red phosporous-free, high-flow FR PC+ABS for EMI/RFI shielding. SE of 21 dB at 1.5 mm.

Physical Properties	Metric	English	Comments
Specific Gravity	1.31 g/cc	1.31 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.00060 - 0.0015 cm/cm @Thickness 3.20 mm	0.00060 - 0.0015 in/in @Thickness 0.126 in	SABIC Method
Linear Mold Shrinkage, Transverse	0.0020 - 0.0040 cm/cm @Thickness 3.20 mm	0.0020 - 0.0040 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	25 g/10 min @Load 1.20 kg, Temperature 300 Â°C	25 g/10 min @Load 2.65 lb, Temperature 572 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	63.0 MPa	9140 psi	Type I, 5 mm/min; ASTM D638
	63.0 MPa	9140 psi	5 mm/min; ISO 527
Tensile Strength, Yield	63.0 MPa	9140 psi	Type I, 5 mm/min; ASTM D638
	63.0 MPa	9140 psi	5 mm/min; ISO 527
Elongation at Break	2.3 %	2.3 %	5 mm/min; ISO 527
	2.4 %	2.4 %	Type I, 5 mm/min; ASTM D638
Elongation at Yield	2.2 %	2.2 %	5 mm/min; ISO 527
	2.3 %	2.3 %	Type I, 5 mm/min; ASTM D638
Tensile Modulus	11.03 GPa	1600 ksi	5 mm/min; ASTM D638
	11.13 GPa	1614 ksi	1 mm/min; ISO 527
Flexural Strength	110 MPa	16000 psi	2 mm/min; ISO 178
	112 MPa	16200 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength	110 MPa	16000 psi	2 mm/min; ISO 178
Flexural Modulus	9.23 GPa	1340 ksi	1.3 mm/min, 50 mm span; ASTM D790
	10.09 GPa	1463 ksi	2 mm/min; ISO 178
Izod Impact, Notched	0.530 J/cm	0.993 ft-lb/in	ASTM D256
Izod Impact, Unnotched	2.24 J/cm	4.20 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	5.00 kJ/mÂ²	2.38 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	15.0 kJ/mÂ²	7.14 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	14.0 J @Temperature 23.0 Â°C	10.3 ft-lb @Temperature 73.4 Â°F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	12.6 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	7.00 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	80.0 Âµm/m-Â°C @Temperature 23.0 - 80.0 Â°C	44.4 Âµin/in-Â°F @Temperature 73.4 - 176 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	63.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	35.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	77.0 Âµm/m-Â°C @Temperature 23.0 - 80.0 Â°C	42.8 Âµin/in-Â°F @Temperature 73.4 - 176 Â°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	98.0 Â°C @Thickness 3.20 mm	208 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	93.0 Â°C @Thickness 3.20 mm	199 Â°F @Thickness 0.126 in	unannealed; ASTM D648
	96.0 Â°C @Thickness 6.40 mm	205 Â°F @Thickness 0.252 in	unannealed; ASTM D648
Vicat Softening Point	100 Â°C	212 Â°F	Rate B/120; ISO 306
	111 Â°C	232 Â°F	Rate B/50; ASTM D1525
UL RTI, Electrical	60.0 Â°C	140 Â°F	UL 746B
UL RTI, Mechanical with Impact	60.0 Â°C	140 Â°F	UL 746B
UL RTI, Mechanical without Impact	60.0 Â°C	140 Â°F	UL 746B
Flammability, UL94	V-0 @Thickness 0.990 mm	V-0 @Thickness 0.0390 in	UL 94

Electrical Properties	Metric	English	Comments
Volume Resistivity	2.0 ohm-cm	2.0 ohm-cm	ASTM D257
Surface Resistance	10000 ohm	10000 ohm	ASTM D257

Users viewing this material also viewed the following: