BASF Polystyrol® 168 N Polystyrene (Europe)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Molded, Unreinforced |
| Manufacturer | BASF |
| Trade Name | Polystyrol® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Polystyrol® 168 N Polystyrene (Europe).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High molecular, heat-resistant grades used where high strength is required. Suitable for expanded film.Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Linear Mold Shrinkage, Flow | 0.0045 cm/cm | 0.0045 in/in | |
| Melt Flow | 1.2 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.2 g/10 min @Load 11.0 lb, Temperature 392 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 59.0 MPa | 8560 psi | |
| Elongation at Break | 3.0 % | 3.0 % | |
| Tensile Modulus | 3.30 GPa | 479 ksi | |
| Charpy Impact Unnotched | 2.80 J/cm² | 13.3 ft-lb/in² | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 3300 MPa | 479000 psi | |
| Tensile Creep Modulus, 1000 hours | 2600 MPa | 377000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 20.0 °C |
44.4 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | |
| Vicat Softening Point | 101 °C | 214 °F | |
| Glass Transition Temp, Tg | 100 °C | 212 °F | |
| Flammability, UL94 | HB @Thickness 3.18 mm |
HB @Thickness 0.125 in |
|
| Oxygen Index | 18 % | 18 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
|
| 2.5 @Frequency 1e+6 Hz |
2.5 @Frequency 1e+6 Hz |
||
| Dissipation Factor | 0.000050 @Frequency 1e+6 Hz |
0.000050 @Frequency 1e+6 Hz |
|
| 0.000090 @Frequency 100 Hz |
0.000090 @Frequency 100 Hz |
||
| Comparative Tracking Index | 475 V | 475 V |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufFill™ 5010UV Polyolefin
- NIZHNEKAMSKNEFTEKHIM PE 4252A (524H1) High Density Polyethylene
- Lubrizol Advanced Materials PEARLBOND® 123 Linear Thermoplastic Polyurethane
- Multibase Multi-Flex® A 7727 HM Black TPE Thermoplastic Elastomer
- SABIC Innovative Plastics SABIC PPCOMPOUND 5521 PP
- SABIC Innovative Plastics LNP LUBRICOMP ZFL24 PPE+PS
- Shakespeare WP-807 diameter 0.2 mm Weft Polyester Monofilament
- Solvay TECHNYL® 27010ST PA66, DRY
- A. Schulman POLYBATCH™ CE-505-B Concentrate Based In Polyethylene
- Dow Corning P5200 ADHESION PROMOTER, CLEAR
Copyright © lookpolymers.com All Rights Reserved