Styrolution Novodur® P2M-V ABS Pellets

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
Manufacturer Styrolution
Trade Name Novodur®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styrolution Novodur® P2M-V ABS Pellets.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Novodur® P2M-V has high impact strength, high gloss, and low emission. It is used for the production of molded plastic articles.
Physical Properties Metric English Comments
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
Test Condition: 60x60x2; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
Test Condition: 60x60x2; ISO 294-4
Melt Flow 18 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 18 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 100 MPa
14500 psi
ISO 2039-1
Tensile Strength, Yield 40.0 MPa
5800 psi
50 mm/min; ISO 527-1,-2
Elongation at Break >= 15 %
>= 15 %
50 mm/min; acc. ISO 527-1,-2
Elongation at Yield 2.2 %
2.2 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 2.30 GPa
334 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 63.0 MPa
9140 psi
2 mm/min; ISO 178
Flexural Modulus 2.20 GPa
319 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 11.0 kJ/m²

@Temperature -30.0 °C
 5.23 ft-lb/in²

@Temperature -22.0 °F
 ISO 180-1A
23.0 kJ/m²

@Temperature 23.0 °C
 10.9 ft-lb/in²

@Temperature 73.4 °F
 ISO 180-1A
Charpy Impact Unnotched 12.0 J/cm²

@Temperature -30.0 °C
 57.1 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eU
18.0 J/cm²

@Temperature 23.0 °C
 85.7 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eU
Charpy Impact, Notched 1.10 J/cm²

@Temperature -30.0 °C
 5.23 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eA
2.20 J/cm²

@Temperature 23.0 °C
 10.5 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eA
Thermal Properties Metric English Comments
CTE, linear 100 µm/m-°C

@Temperature 23.0 - 55.0 °C
 55.6 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1,-2; Parallel to Flow
Deflection Temperature at 0.46 MPa (66 psi) 98.0 °C
208 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
ISO 75-1,-2
Vicat Softening Point 97.0 °C

@Load 5.10 kg
 207 °F

@Load 11.2 lb
 50°C/hour; ISO 306
Flame Spread 55 mm/min

@Thickness 2.00 mm
 2.2 in/min

@Thickness 0.0787 in
 US-FMVSS; ISO 3795
Glow Wire Test 700 °C

@Thickness 2.00 mm
 1290 °F

@Thickness 0.0787 in
 GWFI; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
IEC 60093
Dielectric Constant 2.9

@Frequency 1.00e+6 Hz
 2.9

@Frequency 1.00e+6 Hz
 IEC 60250
3.0

@Frequency 100 Hz
 3.0

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 39.0 kV/mm

@Thickness 1.00 mm
 991 kV/in

@Thickness 0.0394 in
 IEC 60243-1
Dissipation Factor 0.0050

@Frequency 100 Hz
 0.0050

@Frequency 100 Hz
 IEC 60250
0.0080

@Frequency 1.00e+6 Hz
 0.0080

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 600 V
600 V
Solution A, Rating; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 240 °C
464 °F
Injection Molding; ISO 294
Mold Temperature 70.0 °C
158 °F
Injection Molding; ISO 294
Injection Velocity 240 mm/sec
9.45 in/sec
Injection Molding; ISO 294